Hemp and flax fibers are among the most interesting vegetable fibers that can be used to reinforce polymeric matrices. In line with the global environmental requests, the use of these fibers especially coupled with thermoforming polymers are increasing more and more in order to expand their applications and replace synthetic fibers and thermosetting plastics. However, one of the major limitations of vegetable fibers is their poor adhesion with polymeric matrices that is often overcome by fibers chemical treatments or by using coupling agents within the matrix. Aiming to produce polypropylene (PP) bio composite laminates reinforced by hemp and flax fibers without additional process steps, this paper deals on the study of their production via the compression molding technique by using woven fabrics characterized by a large mesh size able to ensure a mechanical anchoring between fibers and matrix. Two different forming strategies that differ in the time required for reaching the maximum values of compression pressure and in the dwelling time at this value were used in order to investigate how the yarn impregnation was affected by them. To expand the applications of composites under investigation, tensile, bending, Izod, heat deflection temperature (HDT) and bearing tests were carried out. The results highlighted how the use of a waiting time before the reaching of the maximum moulding pressure allowed a better matrix flow within the vegetable yarn leading to higher mechanical performances.
Metal foams have a number of established niche market and potential applications under investigation due to their peculiarities including thermal, acoustic and mechanical properties at low weight. In order to produce structures resistant at high temperature and acting as barrier to the fire, metals with closed cells are often required, and one of the most consolidate manufacturing process for their production is the gas releasing particles decomposition in semisolids, by means of which a foam is created by a foaming agent dispersed into a precursor. In previous researches, the authors have investigated the possibility of foaming the aluminum starting by a precursor, placed between two skins consisting of steel grids, in order to obtain a sandwich structure at the same time of the foaming step. In line to continue on this topic and to improve the compression strength of the aluminum-foamed core, in this work the steel grid was used both as skins and as a corrugated skeleton inside the core. Different types of sandwich structures were manufactured, following some experimental tests executed to determine the optimal value of temperature and time to foam the precursor. Then, compression tests were carried out, in order to investigate the effectiveness of the proposed solution on the improvement of this mechanical behavior. The mechanical tests highlighted the increase of mechanical properties using this type of corrugated core.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.