Automatic gas tungsten arc welding experiments of 5083 aluminum alloy were completed, to analyze the weld microstructure and mechanical properties. The influences of welding current, travel speed, frequency, and arc length on weld forming and mechanical properties were studied. When the welding current was 160 A, the travel speed was 380 mm/min, the frequency was 100 Hz, the arc length was 4 mm, and the maximum tensile strength of the welded joint was 296.9 MPa, which was 86.8% of the base metal’s tensile strength. The fracture elongation was 7.8%. No porosity was formed in the weld, but there were poor fusion problems. ER5356 welding wire can improve the problem of poor weld fusion and accommodate Mg element vaporization losses. When the wire feeding speed was 1200 mm/min, the tensile strength of the welded joint can be improved to 315.2 MPa, which was 92.2% of the base material’s tensile strength, and the fracture elongation was 8.5%. The tensile specimens fractured in the heat-affected zone. The fracture surface was characterized as plastic fracture.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.