Metallization layers of aluminum, gold, or copper are shown to be protected from interactions with silicon substrates by thin boron layers grown by chemical-vapor deposition (CVD) at 450 °C. A 3-nm-thick B-layer was studied in detail. It formed the p+-anode region of PureB diodes that have a metallurgic junction depth of zero on n-type Si. The metals were deposited by electron-beam-assisted physical vapor deposition (EBPVD) at room temperature and annealed at temperatures up to 500 °C. In all cases, the B-layer was an effective material barrier between the metal and Si, as verified by practically unchanged PureB diode I–V characteristics and microscopy inspections of the deposited layers. For this result, it was required that the Si surface be clean before B-deposition. Any Si surface contamination was otherwise seen to impede a complete B-coverage giving, sometimes Schottky-like, current increases. For Au, room-temperature interactions with the Si through such pinholes in the B-layer were excessive after the 500 °C anneal.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.