Four mixtures of kaolinite clay and feldspar (Western-Cameroon) were prepared and sintered at 1200 • C for 2 h at the heating rate of 5 • C/min, 10 • C/min, 15 • C/min and 20 • C/min. The main new crystalline phase was mullite associated with quartz, anatase and cristobalite for all heating rates. By increasing the feldspar content, both the amounts of mullite and of glassy phase increase which promotes the densification of the samples. Heating rate has less influence on the formation of new mineral phases, while this process is sensitive to flux content. Both heating rate and flux content have an effect on the microstructure of the fired bodies as well as technological properties. The specimens with 30% feldspar content sintered at 1200 • C from 5 • C/min to 20 • C/min exhibited water absorption values <10% and bending strength >12 MPa. These materials are suitable as wall tiles. Thus, these samples can be sintered at a heating rate of 20 • C/min instead of 5 • C/min which leads to a saving in firing time and in energy.
HAL is a multi-disciplinary open access archive for the deposit and dissemination of scientific research documents, whether they are published or not. The documents may come from teaching and research institutions in France or abroad, or from public or private research centers. L'archive ouverte pluridisciplinaire HAL, est destinée au dépôt et à la diffusion de documents scientifiques de niveau recherche, publiés ou non, émanant des établissements d'enseignement et de recherche français ou étrangers, des laboratoires publics ou privés.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.