Thermal sprayed ethylene methacrylic acid (EMAA) and ethylene tetrafluoroethylene (ETFE) coatings were evaluated for corrosion protection in a biochemical process to treat geothermal residues. Coupon, Atlas cell, peel strength and cathodic disbondment tests were performed in aggressive environments including geothermal sludge, hypersaline brine and sulfur oxidizing bacteria (Thiobacillus jerrooxidans) to determine coating suitability for protecting storage tanks and reaction vessels. It was found that the polymers were resistant to chemical attack and biodegradation at the test temperature of 55°C. The EMAA coatings protected 3l6L stainless steel from corrosion in coupon tests. However, corrosion of mild steel substrates coated with EMAA and ETFE occurred in Atlas cell tests that simulated a lined reactor operating environment and this resulted in decreased adhesive strength. Peel tests revealed that failure mode was dependent on exposure conditions. Cathodic disbondment tests in brine at room temperature indicated that EMAA coatings are resistant to disbondment at applied potentials of -780 to -1070 mV SCE for the test conditions and duration.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.