Sr-containing calcium carbonates were precipitated from solutions containing Ca(OH)2, SrCl2 and Na2CO3 in a reactor where constant solution composition was maintained. The total concentration of divalent ions was same in all experiments, but the Sr/Ca ratio was varied between 0.002 and 0.86, and the pH value was between 12.02 and 12.25. All solutions were oversaturated with respect to calcite (SIcalcite = 1.2-1.5). Calcite was the only product formed at low Sr/Ca ratios, but at Sr/Ca ≥ 0.45 strontianite was detected in some systems. Sr-rich precipitate was observed in both a surface layer on (6.9-6 µm) rhombic calcite seed crystals and as smaller (> 3.64-1.96 µm) calcite crystals that were elongated along their C-axis. The degree of crystal elongation increased with the Sr/Ca ratio in those crystals. Precipitates recovered from low Sr/Ca ratio experiments exhibited an XRD spectrum identical to that of rhombic calcite, however the peaks attributed to Sr-containing calcite shifted progressively to lower 2 values with increasing solution Sr/Ca ratio, indicating increased lattice volume. Sr K-edge EXAFS analysis of the precipitates showed that the shift in morphology and lattice volume is accompanied by a change in the local coordination of Sr 2+ in calcite. The Sr-O bond lengths were similar to the Ca-O bond lengths in calcite, but Sr-O coordination increased from 6 fold in crystals containing 0.21 Wt. % Sr, to 8 fold in crystals containing 9.47 Wt. % Sr, and the Sr-Ca coordination decreased from 6 and 6 (for the first and second Sr-Ca shells respectively) to 4 and 1. It is suggested that Sr 2+ undergoes preferential incorporation at obtuse (+) growth sites on the calcite surface due to its large ionic radius (1.13 Å), and this increases the growth rate parallel to the C-axis, resulting in the observed elongation in this direction.
This study investigated the simultaneous removal of Sr(2+) and (14)CO3(2-) from pH>12 Ca(OH)2 solution by the precipitation of calcium carbonate. Initial Ca(2+):CO3(2-) ratios ranged from 10:1 to 10:100 (mM:mM). Maximum removal of (14)C and Sr(2+) both occurred in the system containing 10mM Ca(2+) and 1mM CO3(2-) (99.7% and 98.6% removal respectively). A kinetic model is provided that describes (14)C and Sr removal in terms of mineral dissolution and precipitation reactions. The removal of (14)C was achieved during the depletion of the initial TIC in solution, and was subsequently significantly affected by recrystallization of the calcite precipitate from an elongate to isotropic morphology. This liberated >46% of the (14)C back to solution. Sr(2+) removal occurred as Ca(2+) became depleted in solution and was not significantly affected by the recrystallization process. The proposed reaction could form the basis for low cost remediation scheme for (90)Sr and (14)C in radioactively contaminated waters (<$0.25 reagent cost per m(3) treated).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.