The Sr0.75La0.25Fe11.75-xCo0.25ZnxO19 hexaferrites are prepared by the ceramic process. Influences of the substitution of Zn2+ ions on crystallographic texture have systematically been investigated by pole figure analysis. The (008) and (107) pole figure shows that the pole intensities are axisymmetric at the center of c axis. With the increase of x, the lattice parameters a and c increase gradually till x=0.15. Excessive Zn2+ addition induces the much coarse grain. The easy-axis alignment of grains decreases from 77.5% to 75.5% for the substitution of Zn2+ ions from 0 to 0.25. When Zn2+ content was from 0 to 0.25, the magnetic properties of Br and (BH)max were increased, while Hcb and Hcj were decreased till x>0.2.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.