We report the physical and mechanical properties of ceramic composite materials fabricated by binder jet 3D printing (BJ3DP) with silicon carbide (SiC) powders, followed by phenolic resin infiltration and pyrolysis (IP) to generate carbon, and a final reactive silicon melt infiltration step. After two phenolic resin infiltration and pyrolysis cycles; porosity was less than 2%, Young's modulus was close to 300 GPa, and the flexural strength was 517.6 ± 24.8 MPa. However, diminishing returns were obtained after more than two phenolic resin infiltration and pyrolysis cycles as surface pores in carbon were closed upon the formation of SiC, resulting in reaction choking and residual-free carbon and porosity. The instantaneous coefficient of thermal expansion of the composite was found to be independent of the number of phenolic IP cycles and had values of between 4.2 and 5.0 ppm/°C between 300 and 1000℃, whereas the thermal conductivity was found to have a weak dependence on the number of phenolic IP cycles. While the manufacturing procedures described here yielded highly dense, gas impermeable, siliconized SiC composites with properties comparable to those of bulk siliconized silicon carbide processed according to conventional techniques, BJ3DP enables the manufacture of objects with complex shape, unlike conventional techniques. K E Y W O R D Sbinder jet 3D printing, phenolic impregnation and pyrolysis, reactive melt infiltration, SiC This manuscript has been authored by UT-Battelle LLC under Contract No. DE-AC05-00OR22725 with the U.S. Department of Energy. The United States Government retains and the publisher, by accepting the article for publication, acknowledges that the United States Government retains a non-exclusive, paid-up, irrevocable, worldwide license to publish or reproduce the published form of this manuscript, or allow others to do so, for United States Government purposes. The Department of Energy will provide public access to these results of federally sponsored research in accordance with the DOE Public Access Plan (http://energy.gov/downl oads/doe-publi c-acces s-plan).

No abstract