Commercial epoxy resin loaded with phosphorus flame retardant led to composites exhibiting remarkable improved flame retardancy and thermal stability.

No abstract

No abstract

A series of thermotropic liquid crystalline aliphatic–aromatic copolyesters derived from various ratios of dodecane‐1,12‐diol (1), terephthaloyl bis‐(4‐oxybenzoyl‐chloride) (2), and 2‐(6‐oxido‐6H‐dibenz〈c,e〉〈1,2〉 oxaphosphorin‐6‐yl)‐1,4‐naphthalene diol (3), has been synthesized. The chemical structures of the monomers and polymers have been confirmed by elemental analyses, and FT‐IR and 1H NMR spectroscopy. The mesomorphic properties of polymers have been investigated by differential scanning calorimetry, polarizing optical microscopy, and X‐ray diffraction measurements. The influence of the content of the aliphatic unit on the phase behavior of the polymers has been examined. The polymers that contain >30 mol‐% aliphatic diol showed smectic phases while the polymers that contained <30 mol‐% aliphatic diol displayed nematic phases. The polymers revealed a reversible mesomorphic phase transition, wide mesophase temperature ranges, and high thermal stability. The degree of crystallinity increased upon increasing the content of aliphatic moieties. The char yield at high temperature increased by increasing the content of phosphorous‐containing bisphenol.magnified image

Silica‐containing polyimide films were prepared by sol‐gel technique using a poly(amic acid) and tetraethoxysilane. The poly(amic acid) was synthesized by solution polycondensation reaction of 4,4′‐oxydiphthalic anhydride with 2,6‐bis(3‐aminophenoxy)benzene and an aminosilane coupling agent, 3‐aminopropyltriethoxysilane. The properties of these films, such as water vapors sorption capacity, dynamic contact angles and contact angle hysteresis, thermal, and electrical behavior have been evaluated with respect to their structure. The polymer films exhibited good thermal stability having the initial decomposition temperature above 450°C, glass transition temperature in the range of 223−228°C, and low‐dielectric constant in the range of 2.64−3.16. Two subglass transitions, γ and β, were evidenced by dynamic mechanical analysis and dielectric spectroscopy. The surface morphology and the roughness were investigated by atomic force microscopy and scanning electron microscopy. POLYM. ENG. SCI., 2010. © 2009 Society of Plastics Engineers

No abstract

No abstract

No abstract