Heritabilities and genetic correlations of economic traits were estimated with a multiple-trait animal model on 5 different strains of Korea Native Chickens (KNC): Red Brown (RB), Yellow Brown (YB), Gray Brown (GB), Black (B) and White (W). The data used for this study were collected from the Daejeon branch of the National Livestock Research Institute and included 11,233 performance records and 12,729 individual animals. DFREML and SAS BASE/STAT packages were used to estimate genetic parameters and descriptive statistics. The estimated heritabilities for strain RB, YB, GB, B and W, respectively, for age at 1st egg were 0.24, 0.27, 0.12, 0.32 and 0.18; for body weight at first egg were 0.39, 0.43, 0.38, 0.52 and 0.57; for body weight at age of 270 days were 0.43, 0.51, 0.30, 0.52 and 0.67; for egg weight at first egg were 0.08, 0.13, 0.07, 0.06 and 0.07; for egg weight at age of 270 days were 0.37, 0.43, 0.22, 0.34 and 0.41; and for number of eggs laid by age of 270 days were 0.24, 0.25, 0.37, 0.36 and 0.30. The genetic and phenotypic correlations were also estimated.

No abstract

Ferromagnetic Cu-doped GaN film was grown on a GaN-buffered sapphire (0001) substrate by a hybrid physical-chemical-vapor-deposition method (HPCVD). The GaCuN film (Cu: 3.6 at.%) has a highly c-axis-oriented hexagonal wurtzite crystal structure, which is similar to GaN buffer but without any secondary phases such as metallic Cu, Cu x N y , and Cu x Ga y compounds. Two weak near-band edge (NBE) emissions at 3.38 eV and donor-acceptor-pair (DAP) transition at 3.2 eV with a typical strong broad yellow emission were observed in photoluminescence spectra for GaN buffer. In contrast, the yellow emission was completely quenched in GaCuN film because Ga vacancies causing the observed yellow emission in undoped GaN were substituted by Cu atoms. In addition, GaCuN film exhibits a blue shift of NBE emission, which could be explained with the +2 oxidation state of Cu ions, replacing +3 Ga ions resulting in band gap increment. The valance sate of Cu in GaCuN film was also confirmed by x-ray photoelectron spectroscopy (XPS) analysis. The GaCuN film shows ferromagnetic ordering and possesses a residual magnetization of 0.12 emu/cm 3 and a coercive field of 264 Oe at room temperature. The unpaired spins in Cu 2+ ions (d 9 ) are most likely to be responsible for the observed ferromagnetism in GaCuN.