Objective-To test the hypothesis that the indentation crack technique can determine surface residual stresses that are not statistically significantly different from those determined from the analytical procedure using surface cracks, the four-point flexure test, and fracture surface analysis.Methods-Soda-lime-silica glass bar specimens (4 mm × 2.3 mm × 28 mm) were prepared and annealed at 650 °C for 30 min before testing. The fracture toughness values of the glass bars were determined from 12 specimens based on induced surface cracks, four-point flexure, and fractographic analysis. To determine the residual stress from the indentation technique, 18 specimens were indented under 19.6 N load using a Vickers microhardness indenter. Crack lengths were measured within 1 min and 24 h after indentation, and the measured crack lengths were compared with the mean crack lengths of annealed specimens. Residual stress was calculated from an equation developed for the indentation technique. All specimens were fractured in a four-point flexure fixture and the residual stress was calculated from the strength and measured crack sizes on the fracture surfaces.Results-The results show that there was no significant difference between the residual stresses calculated from the two techniques. However, the differences in mean residual stresses calculated within 1 min compared with those calculated after 24 h were statistically significant (p=0.003).Significance-This study compared the indentation technique with the fractographic analysis method for determining the residual stress in the surface of soda-lime silica glass. The indentation method may be useful for estimating residual stress in glass.
PURPOSEThe objective was to evaluate canine positions, intercanine tip width (ICTW) and width of distal surface of canine (WDC), related to facial landmarks including interalar width (IAW), intercommissural width (ICoW), and distance between left and right projection lines drawn from inner canthus of eyes to alae of the nose (DPICa) in a group of Thai.MATERIALS AND METHODSOne hundred Thai subjects aged 18-35 years were selected. IAW and ICoW were measured on subject's face using digital vernier caliper. Irreversible hydrocolloid impression of the upper arch was taken, and a cast was poured with dental stone. Silicone impression material was used to take imprint of the incisal edge of upper six anterior teeth. DPICa was obtained from the subject's face using custom-made measuring equipment and marked on the silicone incisal imprint. The marks were then transferred from the imprint to the stone cast and measured with digital caliper. The ICTW and WDC were also measured on the stone cast. Pearson's correlation was used to determine the correlation.RESULTSThe results revealed that the correlation between ICTW-ICoW was 0.429 and ICTW-DPICa was 0.573. The correlation between WDC-ICoW was 0.426 and WDC-DPICa was 0.547. However, IAW did not show any correlation with ICTW or WDC (P>.05).CONCLUSIONThe correlation between canine position and facial landmarks was found. ICTW and WDC had relationship with ICoW and DPICa. DPICa showed stronger correlation with the position of maxillary canine than that of ICoW.
Objective
The objective of this study was to test the null hypothesis that the interfacial toughness of each of two types of bonded core-veneer bilayer ceramics is not significantly different from the apparent fracture toughness of the control monolithic glass veneer.
Methods
T-shaped short bars of a lithia-disilicate glass-ceramic core (LC) and yttria-stabilized polycrystalline zirconia core ceramic (ZC) were prepared according to the manufacturer's recommendations. V-shaped notches were prepared by using 25-μm-thick palladium foil, leaving the chevron notch area exposed, and the bars were veneered with a thermally compatible glass veneer (LC/GV and ZC/GV). Additionally, we also bonded the glass veneer to itself as a control group (GV/GV). Specimens were kept in distilled water for 30 days before testing in tension. Eight glass veneer bars were prepared for the analysis of fracture toughness test using the indentation-strength technique.
Results
The mean interfacial toughness of the LC/GV group was 0.69 [0.11] MPa·m1/2, and did not significantly differ from that of the GV/GV control group, 0.74 (0.17) MPa·m1/2 (p > 0.05). However, the difference between the mean interfacial toughness of the ZC/GV group, 0.13 (0.07) MPa·m1/2, and the LC/GV and the GV/GV groups was statistically significant (p<0.05).
Significance
For bilayer all-ceramic restorations with high-strength core materials, the veneering ceramics are the weakest link in the design of the structure. Since all-ceramic restorations often fail from chipping of veneer layers or crack initiation at the interface, the protective effects of thermal mismatch stresses oral prosthesis design should be investigated.
PURPOSETo compare marginal and internal gaps of zirconia substructure of single crowns with those of three-unit fixed dental prostheses.MATERIALS AND METHODSStandardized Co-Cr alloy simulated second premolar and second molar abutments were fabricated and subsequently duplicated into type-III dental stone for working casts. After that, all zirconia substructures were made using Lava™ system. Marginal and internal gaps were measured in 2 planes (mesial-distal plane and buccal-palatal plane) at 5 locations: marginal opening (MO), chamfer area (CA), axial wall (AW), cusp tip (CT) and mid-occlusal (OA) using Replica technique.RESULTSThere were significant differences between gaps at all locations. The mean ± SD of marginal gap in premolar was 43.6 ± 0.4 µm and 46.5 ± 0.5 µm for single crown and 3-unit bridge substructure respectively. For molar substructure the mean ± SD of marginal gap was 48.5 ± 0.4 µm and 52.6 ± 0.4 µm for single crown and 3-unit bridge respectively. The largest gaps were found at the occlusal area, which was 150.5 ± 0.5 µm and 154.5 ± 0.4 µm for single and 3-unit bridge premolar substructures respectively and 146.5 ± 0.4 µm and 211.5 ± 0.4 µm for single and 3-unit bridge molar substructure respectively.CONCLUSIONIndependent-samples t-test showed significant differences of gap in zirconia substructure between single crowns and three-unit bridge (P<.001). Therefore, the span length has the effect on the fit of zirconia substructure that is fabricated using CAD/CAM technique especially at the occlusal area.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.