We report a facile synthesis of highly monodisperse colloidal Sn and Sn/SnO2 nanocrystals with mean sizes tunable over the range 9-23 nm and size distributions below 10%. For testing the utility of Sn/SnO2 nanocrystals as an active anode material in Li-ion batteries, a simple ligand-exchange procedure using inorganic capping ligands was applied to facilitate electronic connectivity within the components of the nanocrystalline electrode. Electrochemical measurements demonstrated that 10 nm Sn/SnO2 nanocrystals enable high Li insertion/removal cycling stability, in striking contrast to commercial 100-150 nm powders of Sn and SnO2. In particular, reversible Li-storage capacities above 700 mA h g(-1) were obtained after 100 cycles of deep charging (0.005-2 V) at a relatively high current of 1000 mA h g(-1).

Graphite dual-ion batteries represent a potential battery concept for large-scale stationary storage of electricity, especially when constructed free of lithium and other chemical elements with limited natural reserves. Owing to their non-rocking-chair operation mechanism, however, the practical deployment of graphite dual-ion batteries is inherently limited by the need for large quantities of electrolyte solutions as reservoirs of all ions that are needed for complete charge and discharge of the electrodes. Thus far, lithium-free graphite dual-ion batteries have employed moderately concentrated electrolyte solutions (0.3–1 M), resulting in rather low cell-level energy densities of 20–70 Wh kg−1. In this work, we present a lithium-free graphite dual-ion battery utilizing a highly concentrated electrolyte solution of 5 M potassium bis(fluorosulfonyl)imide in alkyl carbonates. The resultant battery offers an energy density of 207 Wh kg−1, along with a high energy efficiency of 89% and an average discharge voltage of 4.7 V.

With demands placed on batteries constantly increasing, new positive electrode materials with higher energy density, satisfactory power density, and long-term cycling capabilities, are desired.