To improve the fatigue resistance of tungsten inert gas (TIG)-welded SS400 steel plates, friction stir processing (FSP) was performed on TIG weld beads. Although the tensile properties of the TIG-welded steel plates with FSP were similar to those without FSP, their bending strength exhibited about 1.4 GPa at room temperature, which was 40% higher than that without FSP (about 1 GPa). Similarly, FSP produced about 170% increase in the number of cycles to failure at an applied stress amplitude of 270 MPa during three-point bending fatigue at room temperature. A fine-grained FSP region (grain sizes of about 1-2 μm in diameter) enhanced grain-boundary strengthening, leading to the higher bending strength and bending fatigue resistance.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.