The slow‐strain‐rate test (SSRT) is the most commonly used method for evaluating pipeline steel in service environments. However, to accurately assess the sensitivity of steel to hydrogen, it is necessary to investigate the effect of different strain rates, taking into account microstructure‐influenced hydrogen migration. Herein, a hot‐rolled X70 pipeline steel sheet is investigated by a SSRT at different strain rates with and without synchronous hydrogen charging. The influence of the pearlite content and different strain rates on the hydrogen‐assisted crack propagation and hydrogen diffusion in pipeline steels is discussed. Using scanning electron microscopy, electron backscatter diffraction, transmission electron microscopy, and hydrogen microprinting, the hydrogen atoms are observed to be easily segregated at the ferrite/pearlite (F/P) interface without external stress. Under loading, a higher strain rate results in lower hydrogen permeation content in steel, penetrating into pearlite and interacting with its internal vacancies, leading to transgranular fracture initiating from pearlite. At a low strain rate, the F/P interface is more vulnerable to hydrogen degradation, leading to intergranular crack mode along the interface and increased tendency to form secondary cracks. Therefore, strain rate–induced crack initiation and propagation characteristics should be considered during the SSRT.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.