The one-step and facile synthesis of multi-enzyme-containing metal-organic framework (MOF) nanocrystals in aqueous solution at 25 °C was reported in this study. The GOx&HRP/ZIF-8 nanocomposite displayed high catalytic efficiency, high selectivity and enhanced stability due to the protecting effect of the framework.
Destructive gas generation with associated swelling has been a major challenge to the large-scale application of lithium ion batteries (LIBs) made from Li4Ti5O12 (LTO) anodes. Here we report root causes of the gassing behavior, and suggest remedy to suppress it. The generated gases mainly contain H2, CO2 and CO, which originate from interfacial reactions between LTO and surrounding alkyl carbonate solvents. The reactions occur at the very thin outermost surface of LTO (111) plane, which result in transformation from (111) to (222) plane and formation of (101) plane of anatase TiO2. A nanoscale carbon coating along with a stable solid electrolyte interface (SEI) film around LTO is seen most effective as a barrier layer in suppressing the interfacial reaction and resulting gassing from the LTO surface. Such an ability to tune the interface nanostructure of electrodes has practical implications in the design of next-generation high power LIBs.
Defects can greatly influence the properties of oxide materials; however, facile defect engineering of oxides at room temperature remains challenging. The generation of defects in oxides is difficult to control by conventional chemical reduction methods that usually require high temperatures and are time consuming. Here, we develop a facile room-temperature lithium reduction strategy to implant defects into a series of oxide nanoparticles including titanium dioxide (TiO2), zinc oxide (ZnO), tin dioxide (SnO2), and cerium dioxide (CeO2). Our lithium reduction strategy shows advantages including all-room-temperature processing, controllability, time efficiency, versatility and scalability. As a potential application, the photocatalytic hydrogen evolution performance of defective TiO2 is examined. The hydrogen evolution rate increases up to 41.8 mmol g−1 h−1 under one solar light irradiation, which is ~3 times higher than that of the pristine nanoparticles. The strategy of tuning defect oxides used in this work may be beneficial for many other related applications.
Uncontrolled growth of lithium dendrites during cycling has remained a challenging issue for lithium metal batteries. Thus far, various approaches have been proposed to delay or suppress dendrite growth, yet little attention has been paid to the solutions that can make batteries keep working when lithium dendrites are already extensively present. Here we develop an industry-adoptable technology to laterally direct the growth of lithium dendrites, where all dendrites are retained inside the compartmented copper current collector in a given limited cycling capacity. This featured electrode layout renders superior cycling stability (e.g., smoothly running for over 150 cycles at 0.5 mA cm−2). Numerical simulations indicate that reduced dendritic stress and damage to the separator are achieved when the battery is abusively running over the ceiling capacity to generate protrusions. This study may contribute to a deeper comprehension of metal dendrites and provide a significant step towards ultimate safe batteries.
The slow kinetics of oxygen evolution reaction (OER) causes high power consumption for electrochemical water splitting. Various strategies have been attempted to accelerate the OER rate, but there are few studies on regulating the transport of reactants especially under large current densities when the mass transfer factor dominates the evolution reactions. Herein, NixFe1–x alloy nanocones arrays (with ≈2 nm surface NiO/NiFe(OH)2 layer) are adopted to boost the transport of reactants. Finite element analysis suggests that the high‐curvature tips can enhance the local electric field, which induces an order of magnitude higher concentration of hydroxide ions (OH−) at the active sites and promotes intrinsic OER activity by 67% at 1.5 V. Experimental results show that a fabricated NiFe nanocone array electrode, with optimized alloy composition, has a small overpotential of 190 mV at 10 mA cm−2 and 255 mV at 500 mA cm−2. When calibrated by electrochemical surface area, the nanocones electrode outperforms the state‐of‐the‐art OER electrocatalysts. The positive effect of the tip‐enhanced local electric field in promoting mass transfer is also confirmed by comparing samples with different tip curvature radii. It is suggested that this local field enhanced OER kinetics is a generic effect to other OER catalysts.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.