A DSC scan of a Cu-33.5Zn-4Sn (mass%) alloy shows two exothermic peaks at around 250 and 300 C. The first peak is associated with the precipitation of 1 -plates with M9R structure, and the second peak is associated with the formation of precipitates. For the first peak, the 1 -plates start to nucleate at grain boundaries and grow dendritically upon heating. The primary and secondary arms of the dendritic 1 -plates grow in two preferred directions, namely, [110] B2 and [100] B2 of the 0 matrix. However, the stacking faults in the two arms are parallel and differ from those with the structure of the twin-accommodating variants. As the thickness and number of 1 -plates increase, the hardness of the alloy increases significantly; however, the recovery strain reduces dramatically. Additionally, the precipitates nucleate heterogeneously at the interface between the 1 -plate and the 0 matrix on heating above 300 C. The volume fraction of the precipitates increases with temperature, resulting in a reduction in the ductility of the alloy and a complete loss of its shape memory effect.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.