Bottom-gate, bottom-contact organic thin film transistors (OTFTs) were fabricated using solvent soluble copper 1,4,8,11,15,18,22,25-octakis(hexyl)phthalocyanine as the active semiconductor layer. The compound was deposited as 70 nm thick spin-coated films onto gold source-drain electrodes supported on octadecyltrichlorosilane treated 250 nm thick SiO 2 gate insulators. The performance of the OTFTs was optimised by investigating the effects of vacuum annealing of the films at temperatures between 50C and 200 C, a range that included the thermotropic mesophase of the bulk material. These effects were monitored by ultraviolet-visible absorption spectroscopy, atomic force microscopy and XRD measurements. Device performance was shown to be dependent upon the annealing temperature due to structural changes of the film. Devices heat treated at 100 C under vacuum ($10 À7 mbar) were found to exhibit the highest field-effect mobility, 0.7 cm 2 V À1 s À1 , with an on-off current modulation ratio of $10 7 , a reduced threshold voltage of 2.0 V and a sub-threshold swing of 1.11 V per decade.
Solution-processed films of 1,4,8,11,15,18,22,25-octakis(hexyl) copper phthalocyanine (CuPc 6 ) were utilized as an active semiconducting layer in the fabrication of organic field-effect transistors (OFETs) in the bottom-gate configurations using chemical vapour deposited silicon dioxide (SiO 2 ) as gate dielectrics. The surface treatment of the gate dielectric with a self-assembled monolayer of octadecyltrichlorosilane (OTS) resulted in values of 4 × 10 −2 cm 2 V −1 s −1 and 10 6 for saturation mobility and on/off current ratio, respectively. This improvement was accompanied by a shift in the threshold voltage from 3 V for untreated devices to −2 V for OTS treated devices. The trap density at the interface between the gate dielectric and semiconductor decreased by about one order of magnitude after the surface treatment. The transistors with the OTS treated gate dielectrics were more stable over a 30-day period in air than untreated ones.
Spin-coated films, approximately 100 nm thick, of a newly synthesized bis[octakis(octyl)phthalocyaninato] lutetium(III) complex on ultrasonically cleaned glass substrates exhibit pronounced chemichromic behaviour with potential application in healthcare. In situ kinetic optical absorption spectroscopic measurements show that the phthalocyanine Q-band is red shifted by 60 nm upon oxidation arising from exposure to bromine vapour. Recovery to the original state is achieved by the treatment of the oxidized films with nicotinamide adenine dinucleotide and L-ascorbic acid (vitamin C) in an aqueous solution containing 1.5 M lithium perchlorate. The neutralization process is found to be governed by first-order kinetics. The linear increase of the reduction rate with increasing concentration of cofactors provides a basis for calibration of analyte concentrations ranging from 3.5 mM down to 0.03 mM.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.