Two-piece implant systems are mainly used in oral implantology involving an osseointegrated implant connected to an abutment, which supports prosthetic structures. It is well documented that the presence of microgaps, biofilms and oral fluids at the implant-abutment connection can cause mechanical and biological complications. The aim of this review paper was to report the degradation at the implant-abutment connection by wear and corrosion processes taking place in the oral cavity. Most of the retrieved studies evaluated the wear and corrosion (tribocorrosion) of titanium-based materials used for implants and abutments in artificial saliva. Electrochemical and wear tests together with microscopic techniques were applied to validate the tribocorrosion behavior of the surfaces. A few studies inspected the wear on the inner surfaces of the implant connection as a result of fatigue or removal of abutments. The studies reported increased microgaps after fatigue tests. In addition, data suggest that micromovements occurring at the contacting surfaces can increase the wear of the inner surfaces of the connection. Biofilms and/or glycoproteins act as lubricants, although they can also amplify the corrosion of the surfaces. Consequently, loosening of the implant-abutment connection can take place during mastication. In addition, wear and corrosion debris such as ions and micro- and nanoparticles released into the surrounding tissues can stimulate peri-implant inflammation that can lead to pathologic bone resorption.

Oral rehabilitation aims to restore the aesthetic and function of the stomatognathic and phonetic systems, providing quality of life for the patients. To reach this objective, dental implants have been applied with high rates of success (Moraschini, Velloso, Luz, & Porto-Barboza, 2015; Nicoli et al., 2017). Nevertheless, placing implants in the correct position by freehand conventional techniques is chal

The aim of this study was to conduct a literature review on the potential benefits with the use of Morse taper dental implant connections associated with small diameter platform switching abutments. A Medline bibliographical search (from 1961 to 2014) was carried out. The following search items were explored: “Bone loss and platform switching,” “bone loss and implant-abutment joint,” “bone resorption and platform switching,” “bone resorption and implant-abutment joint,” “Morse taper and platform switching.” “Morse taper and implant-abutment joint,” Morse taper and bone resorption,” “crestal bone remodeling and implant-abutment joint,” “crestal bone remodeling and platform switching.” The selection criteria used for the article were: meta-analysis; randomized controlled trials; prospective cohort studies; as well as reviews written in English, Portuguese, or Spanish languages. Within the 287 studies identified, 81 relevant and recent studies were selected. Results indicated a reduced occurrence of peri-implantitis and bone loss at the abutment/implant level associated with Morse taper implants and a reduced-diameter platform switching abutment. Extrapolation of data from previous studies indicates that Morse taper connections associated with platform switching have shown less inflammation and possible bone loss with the peri-implant soft tissues. However, more long-term studies are needed to confirm these trends.

This study added important clinical and histological data to contribute in the decision-making process between indication of FGG or ADM.

The aim of this study was to evaluate the density and the morphological aspects of biofilms adhered to different materials applied in oral rehabilitation supported by dental implants. Sixty samples were divided into four groups: feldspar-based porcelain, CoCr alloy, commercially pure titanium grade IV and yttria-stabilized zirconia. Human saliva was diluted into BHI supplemented with sucrose to grow biofilms for 24 or 48 h. After this period, biofilm was removed by 1% protease treatment and then analyzed by spectrophotometry (absorbance), colony forming unit method (CFU.cm-2) and field-emission guns scanning electron microscopy (FEG-SEM). The highest values of absorbance and CFU.cm-2 were recorded on biofilms grown on CoCr alloys when compared to the other test materials for 24 or 48 h. Also, FEG-SEM images showed a high biofilm density on CoCr. There were no significant differences in absorbance and CFU.cm-2 between biofilms grown on zirconia, porcelain and titanium (p<0.05). Microbiological assays associated with microscopic analyses detected a higher accumulation of oral biofilms on CoCr-based materials than that on titanium or zirconia that are used for prosthetic structures.