This study reports on the production of chitosan fibers and 3-D fiber meshes for the use as tissue engineering scaffolds. Both structures were produced by means of a wet spinning technique. Maximum strain at break and tensile strength of the developed fibers were found to be 8.5% and 204.9 MPa, respectively. After 14 d of immersion in simulated body fluid (SBF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and inductively coupled plasma emission (ICP) spectroscopy analyses showed that a bioactive Ca-P layer was formed on the surface of the fibers, meaning that they exhibit a bioactive behavior. The samples showed around 120% max. swelling in physiological conditions. The pore sizes of 3-D chitosan fiber mesh scaffolds were observed to be in the range of 100-500 microm by SEM. The equilibrium-swelling ratio of the developed scaffolds was found to be around 170% (w/w) in NaCl solution at 37 degrees C. Besides that, the limit swelling strain was less than 30%, as obtained by mechanical spectroscopy measurements in the same conditions. The viscoelastic properties of the scaffolds were also evaluated by both creep and dynamic mechanical tests. By means of using short-term MEM extraction test, both types of structures (fibers and scaffolds) were found to be non-cytotoxic to fibroblasts. Furthermore, osteoblasts directly cultured over chitosan fiber mesh scaffolds presented good morphology and no inhibition of cell proliferation could be observed.Osteoblast-like cells proliferating over chitosan based fibers after 7 d of culture.

This work reports the synthesis and characterization of mesoporous silica nanoparticles (MSNs) functionalized with tridecafluorooctyltriethoxysilane (F13) and their in situ incorporation onto cotton textiles. The hybrid MSNs and the functional textiles were prepared by a one-pot co-condensation methodology between tetraethylorthosilicate (TEOS) and F13, with hexadecyltrimethylammonium chloride (CTAC) as the template and triethanolamine as the base. The influence of the F13 to TEOS molar ratio (1:10, 1:5 and 1:3) on the nanoparticle morphology, porosity, degree of functionalization, and hydro/oleophobic properties is discussed. The hybrid nanosilicas presented high colloidal stability and were spherical and monodispersed with average particle size of ∼45 nm. They also showed high surface areas, large pore volumes, and a wormhole-type mesoporous structure. The increase in the organosilane proportion during the co-condensation process led to a more radially branched wormhole-like mesoporosity, a decrease in the surface area, pore volume, and amount of surface silanol groups, and an enrichment of the surface with fluorocarbon moieties. These changes imparted hydrophobic and oleophobic properties to the materials, especially to that containing the highest F13 loading. Cotton textiles were coated with the F13-MSNs through an efficient and less time-consuming route. The combination between surface roughness and mesoporosity imparted by the MSNs, and the low surface energy provided by the organosilane resulted in superhydrophobic functional textiles. Moreover, the textile with the highest loading of fluorocarbon groups was superamphiphobic.

We have studied the influence of oxygen radio frequency glow discharge (RfGD) on the surface and bulk properties of poly(D,L-lactic acid) (PDLLA) and the effect of this surface modification on both protein adsorption and bone cell behavior. PDLLA films were characterized before and after plasma surface modification by water contact angle, surface energy, and adhesion tension of water as well as by scanning electron microscopy (SEM), X-ray electron spectroscopy (XPS), and Fourier transform infra-red (FTIR) spectroscopy. RfGD-films showed an increase in hydrophilicity and surface energy when compared with untreated films. Surface morphological changes were observed by SEM. Chemical analysis indicated significant differences in both atomic percentages and oxygen functional group. Protein adsorption was evaluated by combining solute depletion and spectroscopic techniques. Bovine serum albumin (BSA), fibronectin (FN), vitronectin (VN), and fetal bovine serum (FBS) were used in this study. RfGD-treated surfaces adsorbed more BSA and FN from single specie solutions than FBS that is a more complex, multi-specie solution. MG63 osteoblast-like cells and primary cultures of fetal rat calvarial (FRC) cells were used to assess both the effect of RfGD treatment and protein adsorption on cell attachment and proliferation. In the absence of preadsorbed proteins, cells could not distinguish between treated and untreated surfaces, with the exception of MG63 cells cultured for longer periods of time. In contrast, the adsorption of proteins increased the cells' preference for treated surfaces, thus indicating a crucial role for adsorbed proteins in mediating the response of osteogenic cells to the RfGD-treated PDLLA surface.