An experimental study with an A356-AlSiMgFe alloy was developed to evaluate the microhardness performance in the microstructure resulting of an unsteady-state horizontal solidification process. The Al-7wt%Si-0.3wt%Mg-0.15wt%Fe alloy was elaborated and directionally solidified in a water-cooled horizontal solidification device. In order to experimentally determine the cooling and growth rates (V L and T R , respectively), a thermal analysis was also conducted during solidification. Microstructural characterization by optical microscopy, SEM/EDS elemental mapping and microanalysis of the punctual EDS compositions allowed to observe the presence of an Al-rich dendritic phase (Al (α)) with interdendritic phases second composed of an eutectic mixture: Al (α-eutectic) + Si + Al 8 Mg 3 FeSi 6(π) + Mg 2 Si (θ). Furthermore, the dendritic microstructure was characterized by measuring the secondary dendritic spacings (λ 2) along the horizontally solidified ingot. Higher HV values were observed within the eutectic mixture.

No abstract

No abstract

No abstract

No abstract

No abstract

No abstract

No abstract