We developed a novel <50-microm thick nano-porous bi-layer latex coating for preserving Gluconobacter oxydans, a strict aerobe, as a whole cell biocatalyst. G. oxydans was entrapped in an acrylate/vinyl acetate co-polymer matrix (T (g) approximately 10 degrees C) and cast into 12.7-mm diameter patch coatings (cellcoat) containing approximately 10(9) CFU covered by a nano-porous topcoat. The oxidation of D-sorbitol to L-sorbose was used to investigate the coating catalytic properties. Intrinsic kinetics was studied in microbioreactors using a pH 6.0 D-sorbitol, phosphate, pyruvate (SPP) non-growth medium at 30 degrees C, and the Michaelis-Menten constants determined. By using a diffusion cell, cellcoat and topcoat diffusivities, optimized by arresting polymer particle coalescence by glycerol and/or sucrose addition, were determined. Cryo-FESEM images revealed a two-layer structure with G. oxydans surrounded by <40-nm pores. Viable cell density, cell leakage, and oxidation kinetics in SPP medium for >150 h were investigated. Even though the coatings were optimized for permeability, approximately 50% of G. oxydans viability was lost during cellcoat drying and further reduction was observed as the topcoat was added. High reaction rates per unit volume of coating (80-100 g/L x h) were observed which agreed with predictions of a diffusion-reaction model using parameters estimated by independent experiments. Cellcoat effectiveness factors of 0.22-0.49 were observed which are 20-fold greater than any previously reported for this G. oxydans oxidation. These nano-structured coatings and the possibility of improving their ability to preserve G. oxydans viability may be useful for engineering highly reactive adhesive coatings for multi-phase micro-channel and membrane bioreactors to dramatically increase the intensity of whole-cell oxidations.

Thermostable polymers cast as thin, porous coatings or membranes may be useful for concentrating and stabilizing hyperthermophilic microorganisms as biocatalysts. Hydrogel matrices can be unstable above 65 degrees C. Therefore a 55-microm thick, two layer (cell coat + polymer top coat) bimodal, adhesive latex coating of partially coalesced polystyrene particles was investigated at 80 degrees C using Thermotoga maritima as a model hyperthermophile. Coating permeability (pore structure) was critical for maintaining T. maritima viability. The permeability of bimodal coatings generated from 0.8 v/v of a suspension of non-film-forming 800 nm polystyrene particles with high glass transition temperature (T(g) = 94 degrees C, 26.9% total solids) blended with 0.2 v/v of a suspension of film-forming 158 nm polyacrylate/styrene particles (T(g) approximately -5 degrees C, 40.9% total solids) with 0.3 g sucrose/g latex was measured in a KNO3 diffusion cell. Diffusivity ratio remained above 0.04 (D(eff)/D) when incubated at 80 degrees C in artificial seawater (ASW) for 5 days. KNO3 permeability was corroborated by cryogenic-SEM images of the pore structure. In contrast, the permeability of a mono-dispersed acrylate/vinyl acetate latex Rovace SF091 (T(g) approximately 10 degrees C) rapidly decreased and became impermeable after 2 days incubation in ASW at 80 degrees C. Thermotoga maritima were entrapped in these coatings at a cell density of 49 g cell wet weight/liter of coating volume, 25-fold higher than the density in liquid culture. Viable T. maritima were released from single-layer coatings at 80 degrees C but accurate measurement of the percentage of viable entrapped cells by plate counting was not successful. Metabolic activity could be measured in bilayer coatings by utilization of glucose and maltose, which was identical for latex-entrapped and suspended cells. Starch was hydrolyzed for 200 h by latex-entrapped cells due to the slow diffusion of starch through the polymer top coat compared to only 24 h by suspended T. maritima. The observed reactivity and stability of these coatings was surprising since cryo-SEM images suggested that the smaller low T(g) polyacrylate/styrene particles preferentially bound to the T. maritima toga-sheath during coat formation. This model system may be useful for concentrating, entrapment and stabilization of metabolically active hyperthermophiles at 80 degrees C.

No abstract