The aim of this study was to provide an experimental investigation on the novel method for recycling chips of duplex stainless steel, with the addition of vanadium carbide, in order to produce metal/carbide composites from a high-energy mechanical milling process. Powders of duplex stainless steel with the addition of vanadium carbide were prepared by high-energy mechanical ball milling utilizing a planetary ball mill. For this proposal, experiments following a full factorial design with two replicates were planned, performed, and then analyzed. The four factors investigated in this study were rotation speed, milling time, powder to ball weight ratio and carbide percentage. For each factor, the experiments were conducted into two levels so that the internal behavior among them could be statistically estimated: 250 to 350 rpm for rotation speed, 10 to 50 h for milling time, 10:1 to 22:1 for powder to ball weight ratio, and 0 to 3% carbide percentage. In order to measure and characterize particle size, we utilized the analysis of particle size and a scanning electron microscopy. The results showed with the addition of carbide in the milling process cause an average of reduction in particle size when compared with the material without carbide added. All the four factors investigated in this study presented significant influence on the milling process of duplex stainless steel chips and the reduction of particle size. The statistical analysis showed that the addition of carbide in the process is the most influential factor, followed by the milling time, rotation speed and powder to ball weight ratio. Significant interaction effects among these factors were also identified.
This study aims to analyze the efficiency of niobium and vanadium carbides in the high energy mechanical milling of aluminum bronze alloy. Two series of experiments were made following the same steps for both niobium carbide (NbC) and vanadium carbide (VC) additions: 30 g of chips were weighed and placed in a stainless steel jar with 3 % of carbide and 1 % of stearic acid for a mass/sphere relationship of 1:10. The milling was realized using a planetary ball mill for 10, 30 and 50 hours in an inert argon atmosphere at 300 rpm. Results shown in laser diffraction indicate a great reduction in the particle sizes of powders when VC is used. For 30 hours milling, D50 values ranged from 1580 μm with NbC to 182.3 μm with VC addition. The D50 values ranged from 251.5 μm with NbC to 52.26 μm with VC addition, for 50 hours milling. The scanning electron microscopy showed that in 10 hours of milling, the energy was not sufficient to achieve the shear of chips in both cases. For 30 hours, it's possible to observe particles with sizes between 100 μm and 800 μm with NbC addition while for the same milling time, with VC it's possible to see particles with different sizes, but with many shapes of fine particulates. For 50 hours milling, particles achieved the smaller sizes between 50 and 200 μm with NbC and ranging from 5 until 50 μm with VC addition.Keywords: aluminum bronze; niobium carbide; vanadium carbide; high energy ball milling; powder metallurgy.
Alexandre Nogueira Ottoboni Dias
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.