Barium monoferrite BaFe 2 O 4 classified as permanent magnet stands out among other ceramic magnets due to its high chemical stability, corrosion resistance and low production cost. In addition, experiments conducted on photocatalytic degradation of methyl orange and UV transmittance by spectrophotometry have shown that this material has photocatalytic properties. The spinel ferrite is of importance in many technological areas such as computing, communications and security. Several techniques for synthesis have been studied to optimize the properties of this material. The synthesis of BaFe 2 O 4 by conventional processes often occurs at temperatures above 1000 °C. In this work, we obtained the phase BaFe 2 O 4 at low temperatures (600 °C) from the combustion reaction using nitrates and maleic anhydride as metal complexing agent. Techniques of X-ray diffraction, specific surface area, thermogravimetry analysis and photocatalytic analysis were employed to characterize the products obtained.
ResumoMassas de reparo à quente de sede de válvula e de plugue em panela de aço são utilizadas a fim de se aumentar a vida útil dessas peças, as quais necessitam longo tempo para a troca. Isto propicia um ganho considerável na campanha da panela. O objetivo do presente trabalho foi a caracterização técnica das massas refratárias, bem como a seleção da massa mais adequada para utilização na panela de aço na Usina Rio-grandense. Uma massa magnesiana e duas aluminosas (concretos) foram analisadas por meio de diversas técnicas, como análise de imagens (lupa eletrônica e MEV), distribuição granulométrica, porosidade, composição química, análise mineralógica, resistência à compressão e teste de tração de aderência entre o substrato e a massa. Os resultados demonstraram que a massa de reparo magnesiana com resina de cura à quente apresentou os melhores resultados de adesão junto às sedes, além de apresentar uma significativa resistência à compressão. Palavras-chave: Massas refratárias; Sede de plug; Reparo; Aciaria. CHARACTERIZATION OF UNSHAPED REFRACTORY MATERIALS USED TO REPAIR WELL BLOCKS IN STEEL LADLE AbstractRefractory mixes used for the hot repair of the valve and the plug well blocks increase the lifespan of steel ladles in several campaigns. The extend life of these parts is very important, due to the long time they need to be changed and to return to operation. The objective of this study was the technical characterization of the refractory mixes as well as the selection of the most suitable mix for use in the steel ladle in Rio-grandense plant. A magnesian mass and two aluminous castables were analyzed using various techniques such as image analysis (electronic microscope and SEM), particle size distribution, chemical composition, mineralogical analysis, compressive strength and adhesion tensile test between the substrate and the mix. The results showed that the magnesian repair mass with the hot-cure resin showed the best adhesion results with the well blocks, and provide significant resistance to compression.
RESUMO -O alumínio em estado puro apresenta baixa dureza e resistência mecânica, não servindo para determinadas aplicações. Ocorre, então, a necessidade de combiná-lo com outros metais para aumentar sua utilidade industrial. O alumínio e suas ligas apresentam resistência à corrosão em muitos ambientes e, por essa razão, possuem aplicações industriais importantes. Foi investigada a taxa de corrosão de ligas de Al-3%Cu e Al-5%Cu solidificadas horizontalmente. Ensaios de perda de massa foram obtidos em meio de HCl (0,2 mol.L -1 ), na temperatura de 25 0 C. Ambas as ligas apresentaram menor taxa de corrosão na região próxima à superfície de resfriamento, ou seja, a resistência à corrosão decresceu com o aumento do espaçamento de solidificação.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.