We report a process to form large-area, few-monolayer graphene oxide films and then recover the outstanding mechanical properties found in graphene to fabricate high Young's modulus ( =185 GPa), low-density nanomechanical resonators. Wafer-scale films as thin as 4 nm are sufficiently robust that they can be delaminated intact and resuspended on a bed of pillars or field of holes. From these films, we demonstrate radio frequency resonators with quality factors (up to 4000) and figures of merit ( f x Q>10(11)) well exceeding those of pure graphene resonators reported to date. These films' ability to withstand high in-plane tension (up to 5 N/m) as well as their high Q-values reveals that film integrity is enhanced by platelet-platelet bonding unavailable in pure graphite.

We report the first observation of the n-type nature of hydrogenated graphene on SiO(2) and demonstrate the conversion of the majority carrier type from electrons to holes using surface doping. Density functional calculations indicate that the carrier type reversal is directly related to the magnitude of the hydrogenated graphene's work function relative to the substrate, which decreases when adsorbates such as water are present. Additionally, we show by temperature-dependent electronic transport measurements that hydrogenating graphene induces a band gap and that in the moderate temperature regime [220-375 K], the band gap has a maximum value at the charge neutrality point, is tunable with an electric field effect, and is higher for higher hydrogen coverage. The ability to control the majority charge carrier in hydrogenated graphene, in addition to opening a band gap, suggests potential for chemically modified graphene p-n junctions.

No abstract

We report the fabrication and the operation of nanomechanical resonant structures in nanocrystalline diamond. For this purpose, continuous diamond films as thin as 80 nm were grown using microwave plasma enhanced chemical vapor deposition. The lateral dimensions of the fabricated structures were as small as 50 nm and the measured mechanical resonant frequencies were up to 640 MHz. The mechanical quality factors were in the range of 2500-3000 at room temperature. The elastic properties of these films obtained via the resonant measurements indicate a Young's modulus close to that of single-crystal diamond.

We report a method to introduce direct bonding between graphene platelets that enables the transformation of a multilayer chemically modified graphene (CMG) film from a "paper mache-like" structure into a stiff, high strength material. On the basis of chemical/defect manipulation and recrystallization, this technique allows wide-range engineering of mechanical properties (stiffness, strength, density, and built-in stress) in ultrathin CMG films. A dramatic increase in the Young's modulus (up to 800 GPa) and enhanced strength (sustainable stress ≥1 GPa) due to cross-linking, in combination with high tensile stress, produced high-performance (quality factor of 31,000 at room temperature) radio frequency nanomechanical resonators. The ability to fine-tune intraplatelet mechanical properties through chemical modification and to locally activate direct carbon-carbon bonding within carbon-based nanomaterials will transform these systems into true "materials-by-design" for nanomechanics.