A new epoxy-based ink is reported, which enables 3D printing of lightweight cellular composites with controlled alignment of multiscale, high-aspectratio fiber reinforcement to create hierarchical structures inspired by balsa wood. Young's modulus values up to 10 times higher than existing commercially available 3D-printed polymers are attainable, while comparable strength values are maintained.

Purpose This paper aims to investigate the deposited structure and mechanical performance of printed materials obtained during initial development of the Big Area Additive Manufacturing (BAAM) system at Oak Ridge National Laboratory. Issues unique to large-scale polymer deposition are identified and presented to reduce the learning curve for the development of similar systems. Design/methodology/approach Although the BAAM’s individual extruded bead is 10-20× larger (∼9 mm) than the typical small-scale systems, the overall characteristics of the deposited material are very similar. This study relates the structure of BAAM materials to the material composition, deposition parameters and resulting mechanical performance. Findings Materials investigated during initial trials are suitable for stiffness-limited applications. The strength of printed materials can be significantly reduced by voids and imperfect fusion between layers. Deposited material was found to have voids between adjacent beads and micro-porosity within a given bead. Failure generally occurs at interfaces between adjacent beads and successive layers, indicating imperfect contact area and polymer fusion. Practical implications The incorporation of second-phase reinforcement in printed materials can significantly improve stiffness but can result in notable anisotropy that needs to be accounted for in the design of BAAM-printed structures. Originality/value This initial evaluation of BAAM-deposited structures and mechanical performance will guide the current research effort for improving interlaminar strength and process control.

No abstract

SignificanceNatural composites exhibit hierarchical and spatially varying structural features that give rise to high stiffness and strength as well as damage tolerance. Here, we report a rotational 3D printing method that enables exquisite control of fiber orientation within engineered composites. Our approach broadens their design, microstructural complexity, and performance space by enabling site-specific optimization of fiber arrangements within short carbon fiber–epoxy composites. Using this approach, we have created composites with programmable strain distribution and failure as well as enhanced damage tolerance.

Spiders spin intricate webs that serve as sophisticated prey-trapping architectures that simultaneously exhibit high strength, elasticity and graceful failure. To determine how web mechanics are controlled by their topological design and material distribution, here we create spider-web mimics composed of elastomeric filaments. Specifically, computational modelling and microscale 3D printing are combined to investigate the mechanical response of elastomeric webs under multiple loading conditions. We find the existence of an asymptotic prey size that leads to a saturated web strength. We identify pathways to design elastomeric material structures with maximum strength, low density and adaptability. We show that the loading type dictates the optimal material distribution, that is, a homogeneous distribution is better for localized loading, while stronger radial threads with weaker spiral threads is better for distributed loading. Our observations reveal that the material distribution within spider webs is dictated by the loading condition, shedding light on their observed architectural variations.

No abstract

No abstract

No abstract