This review covers the sustainable development of advanced improvements in CO2 capture and utilization.

No abstract

No abstract

Although photoexcitation has been employed to unlock the low-temperature equilibrium regimes of thermal catalysis, mechanism underlining potential interplay between electron excitations and surface chemical processes remains elusive. Here, we report an associative zinc oxide band-gap excitation and copper plasmonic excitation that can cooperatively promote methanol-production at the copper-zinc oxide interfacial perimeter of copper/zinc oxide/alumina (CZA) catalyst. Conversely, selective excitation of individual components only leads to the promotion of carbon monoxide production. Accompanied by the variation in surface copper oxidation state and local electronic structure of zinc, electrons originating from the zinc oxide excitation and copper plasmonic excitation serve to activate surface adsorbates, catalysing key elementary processes (namely formate conversion and hydrogen molecule activation), thus providing one explanation for the observed photothermal activity. These observations give valuable insights into the key elementary processes occurring on the surface of the CZA catalyst under light-heat dual activation.

No abstract

Copper‐based chalcogenides have been considered as potential photocathode materials for photoelectrochemical (PEC) CO2 reduction due to their excellent photovoltaic performance and favorable conduction band alignment with the CO2 reduction potential. However, they suffer from low PEC efficiency due to the sluggish charge transfer kinetics and poor selectivity, resulting from random CO2 reduction reaction pathways. Herein, a facile heat treatment (HT) of a Cu2ZnSnS4(CZTS)/CdS photocathode is demonstrated to enable significant improvement in the photocurrent density (−0.75 mA cm−2 at −0.6 V vs RHE), tripling that of pristine CZTS, as a result of the enhanced charge transfer and promoted band alignment originating from the elemental inter‐diffusion at the CZTS/CdS interface. In addition, rationally regulated CO2 reduction selectivity toward CO or alcohols can be obtained by tailoring the surficial sulfur vacancies by HT in different atmospheres (air and nitrogen). Sulfur vacancies replenished by O‐doping is shown to favor CO adsorption and the CC coupling pathway, and thereby produce methanol and ethanol, whilst the CdS surface with more S vacancies promotes CO desorption capability with higher selectivity toward CO. The strategy in this work rationalizes the interface charge transfer optimization and surface vacancy engineering simultaneously, providing a new insight into PEC CO2 reduction photocathode design.

Few-layer nitrogen doped graphene was synthesized originating from graphene oxide functionalized by selective oxygenic functional groups (hydroxyl, carbonyl, carboxyl etc.) under hydrothermal conditions, respectively. Transmission electron microscopy (TEM) and atomic force microscopy (AFM) observation evidenced few-layer feature of the graphene oxide. X-ray diffraction (XRD) pattern confirmed phase structure of the graphene oxide and reduced graphene oxide. Nitrogen doping content and bonding configuration of the graphene was determined by X-ray photoelectron spectroscopy (XPS), which indicated that different oxygenic functional groups were evidently different in affecting the nitrogen doping process. Compared with other oxygenic groups, carboxyl group played a crucial role in the initial stage of nitrogen doping while hydroxyls exhibited more evident contribution to the doping process in the late stage of the reaction. Formation of graphitic-like nitrogen species was controlled by a synergistic effect of the involved oxygenic groups (e.g., -COOH, -OH, C-O-C, etc.). The doping mechanism of nitrogen in the graphene was scrutinized. The research in this work may not only contribute to the fundamental understandings of nitrogen doping within graphene but promote the development of producing novel graphene-based devices with designed surface functionalization.

The high ratio of pyridinic and pyridone N-doped graphene sheets have been synthesized by functionalizing graphene oxide (GO) with different oxygen groups on its surface. The typical N-doped graphene was determined to be ~3–5 layers by transmission electron microscopy (TEM) and atomic force microscopy (AFM), and the nitrogen content was measured as 6.8–8 at. % by X-ray photoelectron spectroscopy (XPS). The structure of the N-doped graphene with different surface functional groups was characterized by Raman spectroscopy. The research result indicates that the carboxylation of GO is the key factor to obtain pyridinic and pyridone N types during the N atom doping process. Compared to general N-doped graphene, the electrochemical test shows that specific capacitance of the GO-OOH-N sample reaches up to 217 F/g at a discharge current density 1 A/g and stable cycling performance (keep 88.8 % specific capacitance after 500 cycles at the same discharge current density) when applied to the supercapacitor electrode materials.Electronic supplementary materialThe online version of this article (doi:10.1186/s11671-015-1031-z) contains supplementary material, which is available to authorized users.