Electrospun nanofiber membranes show high potential in various application fields (e.g., filtration, catalysis, and sensing). Nevertheless, knowledge of the mechanical behavior, and more specifically, the deformation of nanofiber membranes is still limited today which can complicate the appliance of nanofiber membranes in applications where they are mechanically loaded. In this paper, we, therefore, analyzed the mechanical behavior of polymeric nanofiber membranes with different fiber orientations (random and aligned) extensively. Polyamide 6 was used as a representative reference polymer for proof-of-concept. Mechanical tests show that all membranes have a coherent deformation behavior at the macroscale up to the point of fracture. Large variations in stiffness, ultimate strength, and ultimate strain were observed between membranes with different fiber orientations (Random: E-mod: 370 ± 34 MP; UTS: 38.5 ± 6.0 MPa; εmax: 30.0 ± 2.8%; Parallel aligned: E-mod: 753 ± 11 MPa; UTS: 55.4 ± 0.8 MPa; εmax: 12.0 ± 0.1%; Perpendicular aligned: E-mod: 24.1 ± 3.7 MPa; UTS:/; εmax: >40%). This shows the versatility and tunability of the mechanical behavior of these nanofiber membranes. At the microscale, the fibrous structure results in deformation mechanisms that resist failure formation and progression when the membrane is mechanically loaded. This results in a high fracture resistance, even for pre-damaged membranes. Realignment of the fibers along the loading direction causes crack tip blunting, locally reinforcing the membrane.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.