Background-Long-term patency of conventional synthetic grafts is unsatisfactory below a 6-mm internal diameter.Poly(⑀-caprolactone) (PCL) is a promising biodegradable polymer with a longer degradation time. We aimed to evaluate in vivo healing and degradation characteristics of small-diameter vascular grafts made of PCL nanofibers compared with expanded polytetrafluoroethylene (ePTFE) grafts. Methods and Results-We prepared 2-mm-internal diameter grafts by electrospinning using PCL (M n ϭ80 000 g/mol).Either PCL (nϭ15) or ePTFE (nϭ15) grafts were implanted into 30 rats. Rats were followed up for 24 weeks. At the conclusion of the follow-up period, patency and structural integrity were evaluated by digital subtraction angiography. The abdominal aorta, including the graft, was harvested and investigated under light microscopy. Endothelial coverage, neointima formation, and transmural cellular ingrowth were measured by computed histomorphometry. All animals survived until the end of follow-up, and all grafts were patent in both groups. Digital subtraction angiography revealed no stenosis in the PCL group but stenotic lesions in 1 graft at 18 weeks (40%) and in another graft at 24 weeks (50%) in the ePTFE group. None of the grafts showed aneurysmal dilatation. Endothelial coverage was significantly better in the PCL group. Neointimal formation was comparable between the 2 groups. Macrophage and fibroblast ingrowth with extracellular matrix formation and neoangiogenesis were better in the PCL group. After 12 weeks, foci of chondroid metaplasia located in the neointima of PCL grafts were observed in all samples. Conclusions-Small-diameter PCL grafts represent a promising alternative for the future because of their better healing characteristics compared with ePTFE grafts. Faster endothelialization and extracellular matrix formation, accompanied by degradation of graft fibers, seem to be the major advantages. Further evaluation of degradation and graft healing characteristics may potentially lead to the clinical use of such grafts for revascularization procedures.

Because of the severe increase of mortality by cardiovascular diseases, there has been rising interest among the tissue-engineering community for small-sized blood vessel substitutes. Here we present small diameter vascular grafts made of slow degradable poly(epsilon-caprolactone) nanofibers obtained by electrospinning. The process was optimized by a factorial design approach that led to reproducible grafts with inner diameters of 2 and 4 mm, respectively. Fiber sizes, graft morphology, and the resulting tensile stress and tensile strain values were studied as a function of various parameters in order to obtain optimal vascular grafts for implantation after gamma-sterilization. The influence of polymer concentration, solvent, needle-collector distance, applied voltage, flow rate, and spinning time has been studied. Consequently, an optimized vascular graft was implanted as an abdominal aortic substitute in nine rats for a feasibility study. Results are given following up a 12-week implantation period showing good patency, endothelization, and cell ingrowth.

No abstract

International audienceAmphiphilic and cationic PCL-based degradable polyester was synthesized by copper-catalyzed azide-alkyne cycloaddition (CuAAC)

No abstract

Background-Clinical small-caliber vascular prostheses are unsatisfactory. Reasons for failure are early thrombosis and late intimal hyperplasia. We thus prepared biodegradable small-caliber vascular prostheses using electrospun polycaprolactone (PCL) with slow-releasing paclitaxel (PTX), an antiproliferative drug. Methods and Results-PCL solutions containing PTX were used to prepare nonwoven nanofibre-based 2-mm ID prostheses. Mechanical morphological properties and drug loading, distribution, and release were studied in vitro. Infrarenal abdominal aortic replacement was carried out with nondrug-loaded and drug-loaded prostheses in 18 rats and followed for 6 months. Patency, stenosis, tissue reaction, and drug effect on endothelialization, vascular remodeling, and neointima formation were studied in vivo. In vitro prostheses showed controlled morphology mimicking extracellular matrix with mechanical properties similar to those of native vessels. PTX-loaded grafts with suitable mechanical properties and controlled drug-release were obtained by factorial design. In vivo, both groups showed 100% patency, no stenosis, and no aneurysmal dilatation. Endothelial coverage and cell ingrowth were significantly reduced at 3 weeks and delayed at 12 and 24 weeks in PTX grafts, but as envisioned, neointima formation was significantly reduced in these grafts at 12 weeks and delayed at 6 months. Conclusions-Biodegradable, electrospun, nanofibre, polycaprolactone prostheses are promising because in vitro they maintain their mechanical properties (regardless of PTX loading), and in vivo show good patency, reendothelialize, and remodel with autologous cells. PTX loading delays endothelialization and cellular ingrowth. Conversely, it reduces neointima formation until the end point of our study and thus may be an interesting option for small caliber vascular grafts.

No abstract

As part of the search of novel degradable polymers, amphiphilic and cationic poly(epsilon-caprolactone)-g-poly(l-lysine) (PCL-g-PlL) copolymers have been synthesized following a grafting "onto" or a grafting "from" method both applied to a macropolycarbanionic PCL derivative. The first approach led to PCL-g-PZlL containing 36% of epsilon-caprolactone and 64% of N-epsilon-Z-l-lysine units, by reaction of activated poly(N-epsilon-Z-l-lysine) on the macropolycarbanion derived from PCL. The second route was based on the anionic ring opening polymerization of N-carboxyanhydride of N-epsilon-benzyloxycarbonyl-l-lysine initiated by the macropolycarbanion derived from PCL and led to a similar copolymer containing 45% of of epsilon-caprolactone and 55% of N-epsilon-Z-l-lysine units. After deprotection of the lysine units, PCL-g-PlL copolymers were obtained. These copolymers are water-soluble and form nanometric micelle-like objects with mean diameters between 60 and 500 nm in distilled water depending on the synthesis route.