Aim: To assess the bonding strength of the Equia Forte resin modified glass ionomer cement to the hybrid composite material by applying different surface treatments.
Methodology: 140 samples as 70 Equia Forte and 70 G-eanial composites were produced as 8 mm diameter 3 mm high cylindrical standardized samples. The samples were divided into 7 groups to treat surfaces. G-eanial composite resins as 4 mm diameter 3 mm high was placed onto the samples and polymerized. Then 1000 thermal cycle was applied and samples were mounted in the universal testing machine. Obtained bond strength values were recorded as Newton. One way Anova and Scheffe post hoc tests were performed for statistics.
Results: In the G-aenial group, the highest bond strength was obtained with laser-bond method (N=17.71, P<0.05) and the lowest bonding strength was obtained with only laser-treated method (N=3.45, P<0.05). In the Equia group, the highest bond strength was obtained with air abrasion-bond method (N=9.29, P<0.05) and the lowest bonding strength was obtained with only laser-treated method (N=0.00, P<0.05).
Conclusion: The fact that sufficient bond strength could not be reached by any surface treatment in Equia Forte may suggest that replacing the Equia Forte instead of repairs may be a better choice.
Vibringe® (Cavex Holland BV, Haarlem, Netherlands), which is marketed by a Dutch company as a sonic washing system, is a system in which manual and sonic activation are combined. It consists of an annular plunger compatible with a 10 ml Luer-lock syringe and a wireless and rechargeable battery. By pressing the button on
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.