As part of the degradation process, it is believed that most plastic debris becomes brittle over time, fragmenting into progressively smaller particles. The smallest of these particles, known as microplastics, have been receiving increased attention because of the hazards they present to wildlife. To understand the process of plastic degradation in an intertidal salt marsh habitat, strips (15.2 cm × 2.5 cm) of high-density polyethylene, polypropylene, and extruded polystyrene were field-deployed in June 2014 and monitored for biological succession, weight, surface area, ultraviolet (UV) transmittance, and fragmentation. Subsets of strips were collected after 4 wk, 8 wk, 16 wk, and 32 wk. After 4 wk, biofilm had developed on all 3 polymers with evidence of grazing periwinkles (Littoraria irrorata). The accreting biofilm resulted in an increased weight of the polypropylene and polystyrene strips at 32 wk by 33.5% and 167.0%, respectively, with a concomitant decrease in UV transmittance by approximately 99%. Beginning at 8 wk, microplastic fragments and fibers were produced from strips of all 3 polymers, and scanning electron microscopy revealed surface erosion of the strips characterized by extensive cracking and pitting. The results suggest that the degradation of plastic debris proceeds relatively quickly in salt marshes and that surface delamination is the primary mechanism by which microplastic particles are produced in the early stages of degradation. Environ Toxicol Chem 2016;35:1632-1640. © 2016 SETAC.

The incidence of microplastics in marine environments has been increasing over the past several decades. The objective of the present study was to characterize the size- and shape-dependent effects of microplastic particles (spheres, fibers, and fragments) on the adult daggerblade grass shrimp (Palaemonetes pugio). Grass shrimp were exposed to 11 sizes of plastic: spheres (30, 35, 59, 75, 83, 116, and 165 μm), fragments (34 and 93 μm), and fibers (34 and 93 μm) at a concentration of 2000 particles/400 mL (= 50 000 particles/L) for 3 h. Following exposure, grass shrimp were monitored for survival, ingested and ventilated microplastics, and residence time. Mortality ranged from 0% to 55%. Spheres and fragments <50 μm were not acutely toxic. Mortality rates in experiments with spheres and fragments >50 μm ranged from 5% to 40%. Mortality was significantly higher in the exposure to 93-μm fibers than other sizes tested (p < 0.001). The shape of the particle had a significant influence on the number of particles ingested by the shrimp (p < 0.001). The residence time of particles in the gut ranged from 27 to 75 h, with an average of 43.0 ± 13.8 h. Within the gills, the residence time ranged from 27 to 45 h, with an average of 36.9 ± 5.4 h. The results suggest that microplastic particles of various sizes and shapes can be ingested and ventilated by adult daggerblade grass shrimp, resulting in acute toxicity. Environ Toxicol Chem 2017;36:3074-3080. © 2017 SETAC.

No abstract

Dentoalveolar injuries are an important and common component of craniomaxillofacial trauma. The dentition serves as a vertical buttress of the face and fractures to this area may result in malalignment of facial subunits. Furthermore, the dentition is succedaneous with 3 phases-primary dentition, mixed dentition, and permanent dentition-mandating different treatment protocols. This article is written for nondental providers to diagnose and treat dentoalveolar injuries.

No abstract