We report the synthesis, structural characterization, and functionality (framework interconversions together with proton conductivity) of an open-framework hybrid that combines Ca(2+) ions and the rigid polyfunctional ligand 5-(dihydroxyphosphoryl)isophthalic acid (PiPhtA). Ca2[(HO3PC6H3COOH)2]2[(HO3PC6H3(COO)2H)(H2O)2]·5H2O (Ca-PiPhtA-I) is obtained by slow crystallization at ambient conditions from acidic (pH ≈ 3) aqueous solutions. It possesses a high water content (both Ca coordinated and in the lattice), and importantly, it exhibits water-filled 1D channels. At 75 °C, Ca-PiPhtA-I is partially dehydrated and exhibits a crystalline diffraction pattern that can be indexed in a monoclinic cell with parameters close to the pristine phase. Rietveld refinement was carried out for the sample heated at 75 °C, Ca-PiPhtA-II, using synchrotron powder X-ray diffraction data, which revealed the molecular formula Ca2[(HO3PC6H3COOH)2]2[(HO3PC6H3(COO)2H)(H2O)2]. All connectivity modes of the "parent" Ca-PiPhtA-I framework are retained in Ca-PiPhtA-II. Upon Ca-PiPhtA-I exposure to ammonia vapors (28% aqueous NH3) a new derivative is obtained (Ca-PiPhtA-NH3) containing 7 NH3 and 16 H2O molecules according to elemental and thermal analyses. Ca-PiPhtA-NH3 exhibits a complex X-ray diffraction pattern with peaks at 15.3 and 13.0 Å that suggest partial breaking and transformation of the parent pillared structure. Although detailed structural identification of Ca-PiPhtA-NH3 was not possible, due in part to nonequilibrium adsorption conditions and the lack of crystallinity, FT-IR spectra and DTA-TG analysis indicate profound structural changes compared to the pristine Ca-PiPhtA-I. At 98% RH and T = 24 °C, proton conductivity, σ, for Ca-PiPhtA-I is 5.7 × 10(-4) S·cm(-1). It increases to 1.3 × 10(-3) S·cm(-1) upon activation by preheating the sample at 40 °C for 2 h followed by water equilibration at room temperature under controlled conditions. Ca-PiPhtA-NH3 exhibits the highest proton conductivity, 6.6 × 10(-3) S·cm(-1), measured at 98% RH and T = 24 °C. Activation energies (Ea) for proton transfer in the above-mentioned frameworks range between 0.23 and 0.4 eV, typical of a Grothuss mechanism of proton conduction. These results underline the importance of internal H-bonding networks that, in turn, determine conductivity properties of hybrid materials. It is highlighted that new proton transfer pathways may be created by means of cavity "derivatization" with selected guest molecules resulting in improved proton conductivity.
Nitrilotris(methylenephosphonic acid) (NTP, [N(CH(2)PO(3)H(2))(3)]) recently has been found to form three-dimensional porous structures with encapsulation of templates as well as layered and linear structures with template intercalation. It was, therefore, of interest to examine the type of organic-inorganic hybrids that would form with metal cations. Mn(II) was found to replace two of the six acid protons, while a third proton bonds to the nitrilo nitrogen, forming a zwitter ion. Two types of compounds were obtained. When the ratio of acid to Mn(II) was less than 10, a trihydrate, Mn[HN(CH(2)PO(3)H)(3)(H(2)O)(3)] (2) formed. Compound 2 is monoclinic P2(1)/c, with a = 9.283(2) A, b = 16.027(3) A, c = 9.7742(2) A, beta = 115.209(3) degrees, V = 1315.0(5) A(3), and Z = 4. The Mn atoms form zigzag chains bridged by two of the three phosphonate groups. The third phosphonate group is only involved in hydrogen bonding. The metal atoms are octahedrally coordinated with three of the sites occupied by water molecules. Adjacent chains are hydrogen-bonded to each other through POH and HN donors, and the additional participation of all the water hydrogens in H-bonding results in a corrugated sheet-like structure. Use of excess NTP at a ratio to metal of 10 to 1 yields an anhydrous compound Mn[HN(CH(2)PO(3)H)(3)] (1), P2(1)/n, a = 9.129(1) A, b = 8.408(1) A, c = 13.453(1) A, beta = 97.830(2) degrees, V = 1023.0(2) A(3), and Z = 4. Manganese is five coordinate forming a distorted square pyramid with oxygens from five different phosphonate groups. The sixth oxygen is 2.85 A from an adjacent Mn, preventing octahedral coordination. All the protonated atoms, three phosphonate oxygens and N, form moderately strong hydrogen bonds in a compact three-dimensional structure. The open-structured trihydrate forms a series of isostructural compounds with other divalent transition metal ions as well as with mixed-metal compositions. This is indicative that the hydrogen bonding controls the type of structure formed irrespective of the cation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.