We report the synthesis, structural characterization, and functionality (framework interconversions together with proton conductivity) of an open-framework hybrid that combines Ca(2+) ions and the rigid polyfunctional ligand 5-(dihydroxyphosphoryl)isophthalic acid (PiPhtA). Ca2[(HO3PC6H3COOH)2]2[(HO3PC6H3(COO)2H)(H2O)2]·5H2O (Ca-PiPhtA-I) is obtained by slow crystallization at ambient conditions from acidic (pH ≈ 3) aqueous solutions. It possesses a high water content (both Ca coordinated and in the lattice), and importantly, it exhibits water-filled 1D channels. At 75 °C, Ca-PiPhtA-I is partially dehydrated and exhibits a crystalline diffraction pattern that can be indexed in a monoclinic cell with parameters close to the pristine phase. Rietveld refinement was carried out for the sample heated at 75 °C, Ca-PiPhtA-II, using synchrotron powder X-ray diffraction data, which revealed the molecular formula Ca2[(HO3PC6H3COOH)2]2[(HO3PC6H3(COO)2H)(H2O)2]. All connectivity modes of the "parent" Ca-PiPhtA-I framework are retained in Ca-PiPhtA-II. Upon Ca-PiPhtA-I exposure to ammonia vapors (28% aqueous NH3) a new derivative is obtained (Ca-PiPhtA-NH3) containing 7 NH3 and 16 H2O molecules according to elemental and thermal analyses. Ca-PiPhtA-NH3 exhibits a complex X-ray diffraction pattern with peaks at 15.3 and 13.0 Å that suggest partial breaking and transformation of the parent pillared structure. Although detailed structural identification of Ca-PiPhtA-NH3 was not possible, due in part to nonequilibrium adsorption conditions and the lack of crystallinity, FT-IR spectra and DTA-TG analysis indicate profound structural changes compared to the pristine Ca-PiPhtA-I. At 98% RH and T = 24 °C, proton conductivity, σ, for Ca-PiPhtA-I is 5.7 × 10(-4) S·cm(-1). It increases to 1.3 × 10(-3) S·cm(-1) upon activation by preheating the sample at 40 °C for 2 h followed by water equilibration at room temperature under controlled conditions. Ca-PiPhtA-NH3 exhibits the highest proton conductivity, 6.6 × 10(-3) S·cm(-1), measured at 98% RH and T = 24 °C. Activation energies (Ea) for proton transfer in the above-mentioned frameworks range between 0.23 and 0.4 eV, typical of a Grothuss mechanism of proton conduction. These results underline the importance of internal H-bonding networks that, in turn, determine conductivity properties of hybrid materials. It is highlighted that new proton transfer pathways may be created by means of cavity "derivatization" with selected guest molecules resulting in improved proton conductivity.

The chemistry of metal phosphonates has been progressing fast with the addition of new materials that possess novel structural features and new properties, occasionally in a cooperative manner. In this paper, we report a new family of functional lanthanide-carboxyphosphonate materials. Specifically, the lanthanide is La, Ce, Pr, Sm, Eu, Gd, Tb, or Dy and the carboxyphosphonate ligand is 2-hydroxyphosphonoacetic acid ( H 3 H P A ) . A l l r e p o r t e d L n H P A c o m p o u n d s , Ln 3 (H 0.75 O 3 PCHOHCOO) 4 •xH 2 O (x = 15−16), crystallize in the orthorhombic system. Two types of structures were isolated: series I and II polymorphs. For both series, the three-dimensional (3D) open frameworks result from the linkage of similar organo-inorganic layers, in the ac-plane, by central lanthanide cations, which yield trimeric units also found in other metal-HPA hybrids. Large oval-shaped 1D channels are formed by the spatial separation of the layers along the b-axis and filled with lattice water molecules. LnHPA materials undergo remarkable crystalline-to-amorphous-to crystalline transformations upon dehydration and rehydration cycles, as confirmed by thermodiffraction and NMR spectroscopy. The highest proton conductivity was observed for GdHPA (series II), 3.2 × 10 −4 S cm −1 at 98% RH and T = 21°C. The dehydration−rehydration chemistry was also followed by photoluminescence spectroscopy. It was shown that loss and reuptake of water molecules are accompanied by clear changes in the photoluminescence spectra and lifetimes of the Eu analog (series II). Our present results reveal a wide family of wellcharacterized, multifunctional lanthanide-based phosphonate 3D-structured metal−organic frameworks (MOFs) that show reversible crystalline-to-amorphous-to-crystalline transformations and, at the same time, exhibit high proton conductivity.

Multifunctional materials, especially those combining two or more properties of interest, are attracting immense attention due to their potential applications. MOFs, metal organic frameworks, can be regarded as multifunctional materials if they show another useful property in addition to the adsorption behavior. Here, we report a new multifunctional light hybrid, MgH(6)ODTMP·2H(2)O(DMF)(0.5) (1), which has been synthesized using the tetraphosphonic acid H(8)ODTMP, octamethylenediamine-N,N,N',N'-tetrakis(methylenephosphonic acid), by high-throughput methodology. Its crystal structure, solved by Patterson-function direct methods from synchrotron powder X-ray diffraction, was characterized by a 3D pillared open framework containing cross-linked 1D channels filled with water and DMF. Upon H(2)O and DMF removal and subsequent rehydration, MgH(6)ODTMP·2H(2)O (2) and MgH(6)ODTMP·6H(2)O (3) can be formed. These processes take place through crystalline-quasi-amorphous-crystalline transformations, during which the integrity of the framework is maintained. A water adsorption study, at constant temperature, showed that this magnesium tetraphosphonate hybrid reversibly equilibrates its lattice water content as a function of the water partial pressure. Combination of the structural study and gas adsorption characterization (N(2), CO(2), and CH(4)) indicates an ultramicroporous framework. High-pressure CO(2) adsorption data are also reported. Finally, impedance data indicates that 3 has high proton conductivity σ = 1.6 × 10(-3) S cm(-1) at T = 292 K at ~100% relative humidity with an activation energy of 0.31 eV.

A new flexible ultramicroporous solid, La(H(5)DTMP)·7H(2)O (1), has been crystallized at room temperature using the tetraphosphonic acid H(8)DTMP, hexamethylenediamine-N,N,N',N'-tetrakis(methylenephosphonic acid). Its crystal structure, solved by synchrotron powder X-ray diffraction, is characterised by a 3D pillared open-framework containing 1D channels filled with water. Upon dehydration, a new related crystalline phase, La(H(5)DTMP) (2) is formed. Partial rehydration of 2 led to La(H(5)DTMP)·2H(2)O (3). These new phases contain highly corrugated layers showing different degrees of conformational flexibility of the long organic chain. The combination of the structural study and the gas adsorption characterization (N(2) and CO(2)) suggests an ultramicroporous flexible framework. NO isotherms are indicative of a strong irreversible adsorption of NO within the pores. Impedance data indicates that 1 is a proton-conductor with a conductivity of 8 × 10(-3) S cm(-1) at 297 K and 98% of relative humidity, and an activation energy of 0.25 eV.

The structural and functional chemistry of a family of alkali-metal ions with racemic R,Shydroxyphosphonoacetate (M-HPAA; M = Li, Na, K, Cs) are reported. Crystal structures were determined by X-ray powder diffraction (Li + ), following an ab initio methodology, or by single crystal (Na + , K + , Cs + ). A gradual increase in dimensionality directly proportional to the alkali ionic radius was observed. [Li 3 (ΟOCCH(OH)PO 3 )(H 2 O) 4 ]⋅H 2 O (Li-HPAA) shows a 1D framework built up by Li-ligand "slabs" with Li + in three different coordination environments (4-, 5-and 6-coordinated). Na-HPAA, Na 2 (ΟOCCH(OH)PO 3 H)(H 2 O) 4 , exhibits a pillared layered "house of cards" structure, while K-HPAA, K 2 (ΟOCCH(OH)PO 3 H)(H 2 O) 2 , and Cs-HPAA, Cs(HΟOCCH(OH)PO 3 H), typically present intricate 3D frameworks. Strong hydrogen bonded networks are created even if no water is present, as is the case in Cs-HPAA. As a result, all compounds show proton conductivity in the range 3.5⋅10 -5 S⋅cm -1 (Cs-HPAA) to 5.6⋅10 -3 S⋅cm -1 (Na-HPAA) at 98 % RH and T = 24 °C. Differences in proton conduction mechanisms, Grothuss (Na + and Cs + ) or vehicular (Li + and K + ) are attributed to the different roles played by water molecules and/or proton transfer pathways between phosphonate and carboxylate groups of the ligand HPAA. Upon slow crystallization, partial enrichment in the S enantiomer of the ligand is observed for Na-HPAA, while the Cs-HPAA is a chiral compound containing only the S enantiomer.