Maleic anhydride was reacted with p-aminophenol and p-toluidine in the presence of di-phosphorus pentoxide (P2O5) as a catalyst to produce two compounds: N-(4-hydroxy-phenyl)maleimide (I) and N-(4-methylphenyl)maleimide (II). The new azo compounds I(a-c) and II(a-c) were prepared by the reaction of I and II with three different aromatic amines, namely aniline, p-aminophenol and p-toluidine. The structures of these compounds were confirmed by CHN, FT-IR, 1H-NMR, 13C-NMR, mass spectrum and UV/Vis spectroscopy.

This chapter explores the characteristic potentials of alkaline sulfite anthraquinone and methanol (ASAM) pulping of bamboo culms (Gigantochloa scortechinii) in the industrial production of pulp and paper for packaging. The biometric characterization results of the bamboo culms show that bamboo has fiber length of 1980-4000 μm, Runkel ratio of 0.86, and flexibility ratio of 50.19, while the chemical compositions of the bamboo contain 47.67% cellulose, 68.33% holocellulose, 26% lignin, and 3.69% solvent extractive, which give good paper quality fiber and also falls within the range of wood from softwoods species. The study revealed that the optimum ASAM pulping parameters was at 16% NaOH and 90 min cooking time, resulting in Kappa number of 14.17 and pulp yield of 49.06%, while the paper tensile index of 20.86 Nm/g, tear index of 22.64 mN.m2/g, and brightness of 39.32% were obtained. The biometric and chemical characterizations of the ASAM pulped bamboo have shown that ASAM pulped bamboo produces high-quality pulp and paper suitable for packaging and printing paper. Hence, the use of bamboo materials can reduce the burden on the forest, due to the increasing demand for paper and paper products, while supporting the natural biodiversity.

Cellulose nanofibers (CNF) were isolated fromGigantochloa scortechiniibamboo fibers using sulphuric acid hydrolysis. This method was compared with pulping and bleaching process for bamboo fiber. Scanning electron microscopy, transmission electron microscopy, Fourier transform infrared spectroscopy, X-ray diffraction, and thermogravimetric analysis were used to determine the properties of CNF. Structural analysis by FT-IR showed that lignin and hemicelluloses were effectively removed from pulp, bleached fibers, and CNF. It was found that CNF exhibited uniform and smooth morphological structures, with fiber diameter ranges from 5 to 10 nm. The percentage of crystallinity was significantly increased from raw fibers to cellulose nanofibers, microfibrillated, along with significant improvement in thermal stability. Further, obtained CNF were used as reinforcement material in epoxy based nanocomposites where tensile strength, flexural strength, and modulus of nanocomposites improved with the addition of CNF loading concentration ranges from 0 to 0.7%.

No abstract