To enhance tribological contacts under cyclic load, high performance materials are required. Utilizing the same high-strength material for the whole machine element is not resource-efficient. In order to manufacture machine elements with extended functionality and specific properties, a combination of different materials can be used in a single component for a more efficient material utilization. By combining different joining techniques with subsequent forming, multi-material or tailored components can be manufactured. To reduce material costs and energy consumption during the component service life, a less expensive lightweight material should be used for regions remote from the highly stressed zones. The scope is not only to obtain the desired shape and dimensions for the finishing process, but also to improve properties like the bond strength between different materials and the microscopic structure of the material. The multi-material approach can be applied to all components requiring different properties in separate component regions such as shafts, bearings or bushes. The current study exemplarily presents the process route for the production of an axial bearing washer by means of tailored forming technology. The bearing washers were chosen to fit axial roller bearings (type 81212). The manufacturing process starts with the laser wire cladding of a hard facing made of martensitic chromium silicon steel (1.4718) on a base substrate of S235 (1.0038) steel. Subsequently, the bearing washers are forged. After finishing, the surfaces of the bearing washers were tested in thrust bearings on an FE-8 test rig. The operational test of the bearings consists in a run-in phase at 250 rpm. A bearing failure is determined by a condition monitoring system. Before and after this, the bearings were inspected by optical and ultrasonic microscopy in order to examine whether the bond of the coat is resistant against rolling contact fatigue. The feasibility of the approach could be proven by endurance test. The joining zone was able to withstand the rolling contact stresses and the bearing failed due to material-induced fatigue with high cycle stability.

The present paper describes a new method concerning the production of hybrid bevel gears using the Tailored Forming technology. The main idea of the Tailored Forming involves the creation of bi-metal workpieces using a joining process prior to the forming step and targeted treatment of the resulting joint by thermo-mechanical processing during the subsequent forming at elevated temperatures. This improves the mechanical and geometrical properties of the joining zone. The aim is to produce components with a hybrid material system, where the high-quality and expensive material is located in highly stressed areas only. When used appropriately, it is possible to reduce costs by using fewer high-performance materials than in a component made of a single material. There is also the opportunity to significantly increase performance by combining special load-tailored high-performance materials. The core of the technology consists in the material-locking coating of semi-finished parts by means of plasma-transferred-arc welding (PTA) and subsequent forming. In the presented investigations, steel cylinders made of C22.8 are first coated with the higher-quality heat-treatable steel 41Cr4 using PTA-welding and then hot-formed in a forging process. It could be shown that the applied coating can be formed successfully by hot forging processes without suffering any damage or defects and that the previous weld structure is completely transformed into a homogeneous forming-typical structure. Thus, negative thermal influences of the welding process on the microstructure are completely neutralized.

Hybrid cylindrical roller thrust bearing washers of type 81212 were manufactured by tailored forming. An AISI 1022M base material, featuring a sufficient strength for structural loads, was cladded with the bearing steel AISI 52100 by plasma transferred arc welding (PTA). Though AISI 52100 is generally regarded as non-weldable, it could be applied as a cladding material by adjusting PTA parameters. The cladded parts were investigated after each individual process step and subsequently tested under rolling contact load. Welding defects that could not be completely eliminated by the subsequent hot forming were characterized by means of scanning acoustic microscopy and micrographs. Below the surface, pores with a typical size of ten µm were found to a depth of about 0.45 mm. In the material transition zone and between individual weld seams, larger voids were observed. Grinding of the surface after heat treatment caused compressive residual stresses near the surface with a relatively small depth. Fatigue tests were carried out on an FE8 test rig. Eighty-two percent of the calculated rating life for conventional bearings was achieved. A high failure slope of the Weibull regression was determined. A relationship between the weld defects and the fatigue behavior is likely.

The current study presents a novel Tailored Forming process chain developed for the production of hybrid bearing bushings. In a first step, semi-finished products in the form of locally reinforced hollow profiles were produced using a new co-extrusion process. For this purpose, a modular tool concept was developed in which a steel tube made of a case-hardening steel, either C15 (AISI 1015) or 20MnCr5 (AISI 5120), is fed laterally into the tool. Inside the welding chamber, the steel tube is joined with the extruded aluminum alloy EN AW-6082. In the second step, sections from the compound profiles were formed into hybrid bearing bushings by die forging. In order to set the required forming temperatures for each material—aluminum and steel—simultaneously, a tailored heating strategy was developed, which enabled successful die forging of the hybrid workpiece to the desired bearing bushing geometry. Using either of the case-hardening steels in combination with aluminum, this novel process chain made it possible to produce intact hybrid bearing bushings, which showed both macroscopically and microscopically intimate material contact inside the compound zone.

No abstract

No abstract

No abstract

The current study introduces a method for manufacturing steel–aluminum bearing bushings by compound forging. To study the process, cylindrical bimetal workpieces consisting of steel AISI 4820 (1.7147, 20MnCr5) in the internal diameter and aluminum 6082 (3.2315, AlSi1MgMn) in the external diameter were used. The forming of compounds consisting of dissimilar materials is challenging due to their different thermophysical and mechanical properties. The specific heating concept discussed in this article was developed in order to achieve sufficient formability for both materials simultaneously. By means of tailored heating, the bimetal workpieces were successfully formed to a bearing bushing geometry using two different strategies with different heating durations. A metallurgical bond without any forging defects, e.g., gaps and cracks, was observed in areas of high deformation. The steel–aluminum interface was subsequently examined by optical microscopy, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). It was found that the examined forming process, which utilized steel–aluminum workpieces having no metallurgical bond prior to forming, led to the formation of insular intermetallic phases along the joining zone with a maximum thickness of approximately 5–7 µm. The results of the EDS analysis indicated a prevailing FexAly phase in the resulting intermetallic layer.