Single crystals of a new oxide, La3Fe(MoO4)6, were grown from fluxes of oxide precursors, and a polycrystalline sample was also prepared by a standard solid state reaction. La3Fe(MoO4)6 crystallizes in the orthorhombic space group Pbca with unit cell parameters a = 19.3164(11), b = 10.4143(5) and c = 22.0594(12) Å. This crystal structure exhibits a singular architectural type built on infinite chains of Fe(MoO4)4, each of them being surrounded by two isolated MoO4 tetrahedra and three isolated La(3+) cations. Fe(3+) ions in La3Fe(MoO4)6 are antiferromagnetically ordered below TN = 6.6 K in chains and between chains, as refined from neutron diffraction data. Further the redox stability of this compound - pure powder - was checked using temperature-programmed X-ray diffraction under a controlled atmosphere; under air, we observed a reversible phase transition above 523 K. The same phenomenon was observed under a reductive atmosphere, followed by a destruction of the as-formed phase above 923 K owing to iron III to II reduction. Reactivity of ethanol was then evaluated to get insights into the redox properties of the material under working conditions. After 4 hours of reaction at 648 K, the ethanol conversion was 97% with a selectivity to acetaldehyde of ∼60%, the other products being formaldehyde (∼10%) and CO2 (∼30%), underlining a better acetaldehyde selectivity than that of the La-free conventional Fe2(MoO4)3 catalytic formulation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.