Guided tissue/bone regeneration (GTR/GBR) is a widely used procedure in contemporary dentistry. To achieve the required results of tissue regeneration, soft tissues that reproduce quickly are separated from the slow-growing bone tissue by membranes. Many types of membranes are currently in use, but none of them fulfil all of the desired features. To address this issue, further research on developing new membranes with better separation characteristics, such as membrane modification, is needed. Many of the current innovative modified materials are still in the phase of in vitro and experimental studies. A collective review on new trends in membrane modification to GTR/GBR is needed due to the widespread use of polymeric membranes and the constant development in the field of dentistry. Therefore, the aim of this review was to present an overview of polymeric membrane modifications to the GTR/GBR reported in the literature. The authors searched databases, including PubMed, SCOPUS, Web of Science, and OVID, for relevant studies that were published during 1999–2019. The following keywords were used: guided tissue regeneration, membranes, coating, and modification. A total of 17 papers were included in this review. Furthermore, the articles were divided into three groups that were based on the type of membrane modification: antibiotic coating, ion-use modifications, and others modifications, thus providing an overview of current existing knowledge in the field and encouraging further research. The results of included studies on modified barrier membranes seem to be promising, both in terms of safety and benefits for patients. However, modifications result in a large spectrum of effects. Further clinical studies are needed on a large group of patients to clearly confirm the effects that were observed in animal and in vitro studies.
Temporomandibular disorders (TMD) have multifactorial and complex etiology. Regardless of their etiology, all those conditions may result in centrally mediated chronic muscle pain, myalgia, myofascial pain, myofibrotic contracture, myosistis, myospasm, headache and a variety of neck, shoulder, upper back and lower back pain. Biofeedback (BF) is one of methods that has been used for more than 50 years in rehabilitation to facilitate normal movement patterns after injuries. Some studies suggest that biofeedback may be an effective treatment option for patients with different muscle disorders. The aim of this study was to evaluate the efficiency of biofeedback in masticatory muscle activity management in the light of current medical literature. The authors followed the Preferred Reporting Items for Systematic Review and Meta-Analysis (PRISMA) guidelines for this systematic review. The authors searched the MEDLINE, Scopus, Web of Science, CINAHL databases to identify relevant publications. Finally 10 papers were included. Most of the selected studies showed a significant correlation between biofeedback usage and reduction of masticatory muscle activity. By analyzing qualified studies, it can be concluded that biofeedback can be an effective tool in masticatory muscle activity management.
The aim of the study was to evaluate the influence of thermocycling on the shear bond strength of self-adhesive, self-etching resin cements luted to human dentin and computer-aided design/computer-aided manufacturing (CAD/CAM) ceramics. Three modern self-adhesive dental cements (Maxcem Elite, RelyX U200, Panavia SA) were used to lute three CAD/CAM ceramics (IPS Empress CAD, IPS e.max CAD, IPS e.max ZirCAD) onto the dentin. One conventional cement (Panavia V5) served as a control. After preparation, the samples were subjected to thermocycling as a method of artificial aging of dental materials applied to simulate long-term use in oral conditions. Shear bond strength was evaluated according to PN-EN ISO 29022:2013-10 and failure modes were observed under a light microscope. Statistical analysis was performed. The study demonstrated that a combination of ceramics and cements directly impacts the bond strength. The highest bond strength was observed in Panavia V5, lower in Panavia SA and Maxcem Elite and the lowest–in RelyX U200. Adhesive failure between human dentin and cements was the most common failure mode. Moreover, thermocycling highly decreased bond strength of self-adhesive, self-etching cements.
(1) The CAD/CAM technique exploiting 3D printing is becoming more and more popular in dentistry. The resins are used in all the dental specialties, including conservative dentistry, prosthodontics, surgery, and orthodontics. The interest in investigating the different properties of dental materials has been an aim of researchers. The purpose of the presented study was to compare the properties of two 3D-printable dental resins (both rigid, used for medical purposes). (2) Methods: Ten blocks of two-type shapes were printed on a printer designed for medical use. The tensile modulus and compression were investigated and compared. The axial compression test was performed according to the PN-EN ISO 604:2003 norm, while the tensile test was performed according to the PN-En ISO 527-1-2019 (E) norm. In the first test, the sample size of the perpendicular shape was 10 ± 0.2 mm × 10 ± 0.2 mm × 4 ± 0.2 mm and in the second it was 75 mm, the end width 10 mm, and the thickness 2 mm. (3) Results: The statistical analysis based on ANOVA tests showed that all the obtained results were statistically significant. Both of the examined materials had similar properties and were resistant and stable in shape. The tensile modulus and compression tests performed on them gave similar results. They also showed high durability to compression and tensility. (4) Conclusions: Both of the examined materials were durable and rigid materials. BioMed Amber was more resistant to compression, while Dental LT clear was more resistant in the tensility test. Although both resins had similar physical properties, it is still disputable whether the chosen materials could be used interchangeably.
Purpose: The aim of the study was to evaluate the shear bond strength of CAD/CAM ceramics to dentin after cementation with conventional or self-adhesive resin cements. Methods: Three self-adhesive, self-etching cements (Panavia SA, RelyX U200, Maxcem Elite), and one conventional cement (Panavia V5), were selected to lute three CAD/CAM ceramics (IPS Empress CAD, IPS e.max CAD, IPS e.max ZirCAD) onto the dentin. The bond strength was evaluated using a shear strength test according to the PN-EN ISO 29022:2013-10. Evaluation of the differences was performed using the Statistica software. Failure modes were analyzed using a light microscope. Results: All the studied cements differed (regardless of the ceramic type) in the bond strength. The highest bond strength was observed in Panavia V5, lower – in RelyX U200 and Panavia SA, and the lowest – in Maxcem. For IPS e.max ZirCAD, it was observed that compared to Panavia V5, the other cements were characterized by a significantly higher bond strength. For the IPS Empress CAD and the IPS e.max CAD, Panavia V5 displayed the highest bond strength. For all the studied self-adhesive cements, the failure of adhesion between the cement and dentin was predominant mode. Conclusions: Significant differences were found in the shear bond strengths of the CAD/CAM ceramics luted to dentin using tested self-adhesive and conventional cements. The bond strength depended on the combination of ceramic and cement. The IPS e.max ZirCAD had the highest bond strength to dentin after cementation with RelyX U200, while the IPS Empress CAD and IPS e.max CAD – with Panavia V5.
There is an ongoing search for novel disinfection techniques that are not only effective, cheap, and convenient, but that also do not have adverse effects on the properties of dental impressions. We compared the effects of various methods (UVC, gaseous ozone, commercial solution, and spray) on the dimensional change, tensile strength, and hardness of silicone impressions. Moreover, as a secondary aim, we performed a statistical comparison of the properties of nondisinfected addition (Panasil Putty Soft, Panasil monophase Medium, Panasil initial contact Light) and condensation silicones (Zetaplus Putty and Oranwash L), as well as a comparison of materials of various viscosities (putty, medium-bodied, and light-bodied). Our results revealed that addition silicones had higher dimensional stability, tensile strength, and Shore A hardness compared to condensation silicones. Both traditional (immersion and spraying) and alternative methods of disinfection (UVC and ozone) had no significant impact on the tensile properties and dimensional stability of the studied silicones; however, they significantly affected the hardness, particularly of Oranwash L. Our study demonstrated that, similarly to standard liquid disinfectants, both UVC and ozone do not strongly affect the material properties of most silicones. However, before recommendation, their usefulness for each individual material should be thoroughly evaluated.
Shear wave elastography (SWE) is an objective and reliable method for the assessment of muscles and internal organs. Every organ exhibits its own stiffness characteristics and hence requires individual reference values. We aimed to determine the reference values of stiffness of the masseter muscle in healthy adult individuals using SWE. We analyzed the data of 140 participants (74 men, 66 women) with a median age of 50 years. The overall mean elasticity was 10.67 ± 1.77 kPa. The average values were lower by 2.25 kPa (9.15%) in women compared to men (9.48 ± 1.47 kPa vs. 11.73 ± 1.27 kPa; p < 0.0001). The values of stiffness increased with age, with a correlation coefficient of about 0.35 and a p < 0.0001. Age was a significant influencing factor of masseter muscle stiffness. The left and right masseters had similar stiffness. We conclude that stiffness values are significantly lower in women than in men with a difference of 9%. Age significantly influences the stiffness of masseter muscle, and the values of stiffness increase significantly with age, particularly in men. However, further studies are required to determine the precise ranges of stiffness accounting for age and sex in healthy subjects and people with disorders and conditions of the masticatory system.
For long-term successful use of ceramic materials in dental procedures, it is necessary to ensure reliable bonding of restorations to dental substrates. This can be achieved by the application of a proper luting cement and through additional surface conditioning. The present systematic review summarizes the most up-to-date evidence on the use of different surface modification methods to enhance the bond strength of dental ceramics to the hard tissues of the teeth. The authors of the review searched the Web of Science, Scopus, and MEDLINE databases to identify relevant articles published between 1 January 2010 and 1 January 2020. A total of 4892 records were identified, and after screening, the full text of 159 articles was evaluated, which finally resulted in the inclusion of 19 studies. The available reports were found to be heterogeneous in terms of materials and methodology, and therefore, only within-studies comparison was performed instead of comparison between studies. A statistically significant difference in the bond strength between the samples treated with different methods of surface conditioning, or between conditioned and nonconditioned samples, was revealed by most of the studies. Predominantly, the studies showed that a combination of mechanical and chemical methods was the most effective way of enhancing bond strength. Artificial aging and luting cement were also identified as the factors significantly influencing bond strength.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.