Electronic-type-separated SWCNTs thin-films were used to demonstrate that the strength of the redox potential of dopants influences their electrical conductivity enhancement.
Single-wall carbon nanotubes (SWCNTs) synthesized via laser vaporization have been dispersed using chlorosulfonic acid (CSA) and extruded under varying coagulation conditions to fabricate multifunctional wires. The use of high purity SWCNT material based upon established purification methods yields wires with highly aligned nanoscale morphology and an over 4× improvement in electrical conductivity over as-produced SWCNT material. A series of eight liquids have been evaluated for use as a coagulant bath, and each coagulant yielded unique wire morphology based on its interaction with the SWCNT-CSA dispersion. In particular, dimethylacetamide as a coagulant bath is shown to fabricate highly uniform SWCNT wires, and acetone coagulant baths result in the highest specific conductivity and tensile strength. A 2× improvement in specific conductivity has been measured for SWCNT wires following tensioning induced both during extrusion via increased coagulant bath depth and during solvent evaporation via mechanical strain, over that of as-extruded wires from shallower coagulant baths. Overall, combination of the optimized coagulation parameters has yielded acid-doped wires with the highest reported room temperature electrical conductivities to date of 4.1-5.0 MS/m and tensile strengths of 210-250 MPa. Such improvements in bulk electrical conductivity can impact the adoption of metal-free, multifunctional SWCNT materials for advanced cabling architectures.
A process to fabricate carbon nanotube (CNT) wires with diameters greater than 1 cm and continuous current carrying capability exceeding 20 A is demonstrated. Wires larger than 5 mm are formed using a multi-step radial densification process that begins with a densified CNT wire core followed by successive wrapping of additional CNT material to increase the wire size. This process allows for a wide range of wire diameters to be fabricated, with and without potassium tetrabromoaurate (KAuBr4) chemical doping, and the resulting electrical and thermal properties to be characterized. Electrical measurements are performed with on/off current steps to obtain the maximum current before reaching a peak CNT wire temperature of 100 °C and before failure, yielding values of instantaneous currents in excess of 45 A for KAuBr4 doped CNT wires with a diameter of 6 mm achieved prior to failure. The peak temperature of the wires at failure (∼530 °C) is correlated with the primary decomposition peak observed in thermal gravimetric analysis of a wire sample confirming that oxidation is the primary failure mode of CNT wires operated in air. The in operando stability of doped CNT wires is confirmed by monitoring the resistance and temperature, which remain largely unaltered over 40 days and 1 day for wires with 1.5 mm and 11.2 mm diameters, respectively. The 100 °C continuous current rating, or ampacity, is measured for a range of doped CNT wire diameters and corresponding linear mass densities ρL. To describe the results, a new form of the fuse-law, where the critical current is defined as I∝ρL3/4, is developed and shows good agreement with the experimental data. Ultimately, CNT wires are shown to be stable electrical conductors, with failure current densities in excess of 50 A in the case of a convectively cooled 11.2 mm doped CNT wire, and amenable for use in applications that have long-term, high-current demands.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.