̀This paper reports on the advancement of magnetic ionic liquids (MILs) as stable dispersions of surface-modified γ-Fe(2)O(3), Fe(3)O(4), and CoFe(2)O(4) magnetic nanoparticles (MNPs) in a hydrophobic ionic liquid, 1-n-butyl 3-methylimidazolium bis(trifluoromethanesulfonyl)imide (BMI.NTf(2)). The MNPs were obtained via coprecipitation and were characterized using powder X-ray diffraction, transmission electron microscopy, Raman spectroscopy and Fourier transform near-infrared (FT-NIR) spectroscopy, and magnetic measurements. The surface-modified MNPs (SM-MNPs) were obtained via the silanization of the MNPs with the aid of 1-butyl-3-[3-(trimethoxysilyl)propyl]imidazolium chloride (BMSPI.Cl). The SM-MNPs were characterized by Raman spectroscopy and Fourier transform infrared-attenuated total reflectance (FTIR-ATR) spectroscopy and by magnetic measurements. The FTIR-ATR spectra of the SM-MNPs exhibited characteristic absorptions of the imidazolium and those of the Fe-O-Si-C moieties, confirming the presence of BMSPI.Cl on the MNP surface. Thermogravimetric analysis (TGA) showed that the SM-MNPs were modified by at least one BMSPI.Cl monolayer. The MILs were characterized using Raman spectroscopy, differential scanning calorimetry (DSC), and magnetic measurements. The Raman and DSC results indicated an interaction between the SM-MNPs and the IL. This interaction promotes the formation of a supramolecular structure close to the MNP surface that mimics the IL structure and is responsible for the stability of the MIL. Magnetic measurements of the MILs indicated no hysteresis. Superparamagnetic behavior and a saturation magnetization of ~22 emu/g could be inferred from the magnetic measurements of a sample containing 50% w/w γ-Fe(2)O(3) SM-MNP/BMI.NTf(2).
This paper aims at the synthesis of a new type of elastomers from caryophyllene. The adopted strategy was to cross-link the polycaryophyllene, which was synthesized by ring-opening metathesis polymerization (ROMP). The polycaryophyllene obtained showed Mn = 2 x 10 4 g.mol-1 (Đ = 1.5) with a glass transition temperature (Tg) of-35 °C. On the first hand, thermal cross-linking was performed in the presence of organic peroxides or sulfur system. On the second hand, thiol-ene coupling initiated by UV-light at room temperature was also investigated as an alternative pathway to cross-link the polycaryophyllene. The materials obtained were analyzed by TGA, DSC, and DMA. The Tg of cross-linked polycaryophyllene could be easily modulated from-35 °C to a range between-25 and 10 °C by changing the type of cross-linking agent. The curing process led to the improvement of thermal stability ranging from 200 °C to around 340 °C. Finally, the network storage modulus varied from 1 to 100 MPa at room temperature.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.