Mesoporous silica monoliths were prepared by the sol-gel technique and filled with 1-ethyl-3-methyl imidazolium [Emim]-X (X=dicyanamide [N(CN)2], ethyl sulfate [EtSO4], thiocyanate [SCN], and triflate [TfO]) ionic liquids (ILs) using a methanol-IL exchange technique. The structure and behavior of the ILs inside the silica monoliths were studied using X-ray scattering, nitrogen sorption, IR spectroscopy, solid-state NMR, and thermal analysis. DSC finds shifts in both the glass transition temperature and melting points (where applicable) of the ILs. Glass transition and melting occur well below room temperature. There is thus no conflict with the NMR and IR data, which show that the ILs are as mobile at room temperature as the bulk (not confined) ILs. The very narrow line widths of the NMR spectra suggest that the ILs in our materials have the highest mobility reported for confined ILs so far. As a result, our data suggest that it is possible to generate IL/silica hybrid materials (ionogels) with bulk-like properties of the IL. This could be interesting for applications in, e.g., the solar cell or membrane fields.

No abstract

The current paper shows that poly(ethylene imine) (PEI) is an efficient template for the fabrication of spherical calcium phosphate (CaP)/polymer hybrid particles at pH values above 8. The polymer forms spherical entities, which contain one or a few CaP particles with diameters of ca. 6 nm. The samples contain up to 20 wt % polymer, which appears to be wrapped around the small CaP particles. The particles form via a mineralization-trapping pathway, where at the beginning of the precipitation small CaP particles form. Further particle growth is then prevented by precipitation of the PEI onto these particles at pH values of ca. 8. Stabilization of the particles is provided by the re-protonation of the PEI, which is adsorbed on the CaP particles, during the remainder of the mineralization process. At low pH, much larger particles form. They most likely grow via heterogeneous nucleation and growth on existing, polymermodified CaP surfaces.