We demonstrate that the action of physical pressure, chemical compression, or aliovalent substitution in ACo2As2 (A = Eu and Ca) has a general consequence of causing these antiferromagnetic materials to become ferromagnets. In all cases, the mixed valence triggered at the electropositive A site results in the increase of the Co 3d density of states at the Fermi level. Remarkably, the dramatic alteration of magnetic behavior results from the very minor (<0.15 electron) change in the population of the 3d orbitals. The mixed valence state of Eu observed in the high-pressure (HP) form of EuCo2As2 exhibits a remarkable stability, achieving the average oxidation state of +2.25 at 12.6 GPa. In the case of CaCo2As2, substituting even 10% of Eu or La into the Ca site causes ferromagnetic ordering of Co moments. Similar to HP-EuCo2As2, the itinerant 3d ferromagnetism emerges from electronic doping into the Co layer because of chemical compression of Eu sites in Ca0.9Eu0.1Co1.91As2 or direct electron doping in Ca0.85La0.15Co1.89As2. The results reported herein demonstrate the general possibility of amplifying minor localized electronic effects to achieve major changes in material's properties via involvement of strongly correlated electrons.

No abstract

Four rare-earth cobalt arsenides, RCo 2 As 2 (R = La, Ce, Pr, Nd), were obtained by reactions of constituent elements in molten Bi. The use of Bi flux also allowed the growth of representative single crystals. All compounds are isostructural and belong to the ThCr 2 Si 2 type (space group I4/mmm). The formation of Co vacancies is observed in all structures, while the structures of La-and Ce-containing compounds also show incorporation of minor Bi defects next to the R crystallographic site. Correspondingly, the general formula of these materials can be written as R 1−x Bi x Co 2−δ As 2 , with x/δ = 0.03/0.1, 0.05/0.15, 0/0.2, and 0/0.3 for R = La, Ce, Pr, and Nd, respectively. All compounds exhibit high-temperature ferromagnetic ordering of Co magnetic moments in the range 60−200 K. Electronic band structure calculations revealed a high peak in the density of states at the Fermi level, thus supporting the itinerant nature of magnetism in the Co sublattice. The magnetic ordering in the lanthanide sublattice takes place at lower temperatures, with the R moments aligning antiparallel to the Co moments to give a ferrimagnetic ground state. The measurements on oriented single crystals demonstrated significant magnetic anisotropy in the ferrimagnetic state, with the preferred moment alignment along the c axis of the tetragonal lattice. Neutron powder diffraction failed to reveal the structure of magnetically ordered states but confirmed the presence of Co vacancies. X-ray absorption near-edge structure spectroscopy on Ce 1.95 Bi 0.05 Co 1.85 As 2 showed the average oxidation state of Ce to be +3.06. Solid state NMR spectroscopy revealed a substantially reduced hyperfine field on the Co atoms in the vicinity of Bi defects.