The controlled double‐sensitivity of stimuli‐responsive polymers (see figure) can be used to adjust their functional properties. The ion or solvent concentration, automatically controlled by the micro‐chemostat, is adjusted by the temperature of a thermosensitive hydrogel corresponding to its phase transition concentration.
Abstract:The conducting polymer PEDOT (poly-3,4-ethylenedioxythiophene) has been polymerized onto 3 mm and 10 µm electrodes from a propylene carbonate solution. The electrodes have then been tested in a Chardonnay wine, including dilutions in a model wine solution, with comparisons made to scans with a glassy carbon electrode. A well-defined oxidation peak was obtained for the white wine at PEDOT in the 400 to 450 mV (Ag/AgCl) range, where peaks were also obtained for the representative phenolics caffeic acid and catechin. The voltammetry at PEDOT was typical of a surface-confined process. Significant preconcentration, leading to an increased current response, was noted over a period of 20 min of holding time. Extensive PEDOT growth was observed in the microelectrode case, leading to current densities for the oxidation of caffeic acid over 1000 times greater than those observed at the macroelectrode, matching the high surface area and fractal-type growth observed in SEM images.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.