An efficient process is developed by spin‐coating a single‐component, self‐assembled monolayer (SAM) to simultaneously modify the bottom‐contact electrode and dielectric surfaces of organic thin‐film transistors (OTFTs). This effi cient interface modifi cation is achieved using n‐alkyl phosphonic acid based SAMs to prime silver bottom‐contacts and hafnium oxide (HfO2) dielectrics in low‐voltage OTFTs. Surface characterization using near edge X‐ray absorption fi ne structure (NEXAFS) spectroscopy, X‐ray photoelectron spectroscopy (XPS), attenuated total reflectance Fourier transform infrared (ATR‐FTIR) spectroscopy, atomic force microscopy (AFM), and spectroscopic ellipsometry suggest this process yields structurally well‐defi ned phosphonate SAMs on both metal and oxide surfaces. Rational selection of the alkyl length of the SAM leads to greatly enhanced performance for both n‐channel (C60) and p‐channel (pentacene) based OTFTs. Specifi cally, SAMs of n‐octylphos‐phonic acid (OPA) provide both low‐contact resistance at the bottom‐contact electrodes and excellent interfacial properties for compact semiconductor grain growth with high carrier mobilities. OTFTs based on OPA modifi ed silver electrode/HfO2 dielectric bottom‐contact structures can be operated using < 3V with low contact resistance (down to 700 Ohm‐cm), low subthreshold swing (as low as 75 mV dec−1), high on/off current ratios of 107, and charge carrier mobilities as high as 4.6 and 0.8 cm2 V−1 s−1, for C60 and pentacene, respectively. These results demonstrate that this is a simple and efficient process for improving the performance of bottom‐contact OTFTs.

The objective of this study is to determine whether a residual moisture analyzer (RMA) can be an acceptable instrument for measuring the residual moisture in lyophilized demineralized bone matrix (DBM). Instruments from two different manufacturers with differing configurations and controls were compared: the Ohaus MB45 and Arizona Instrument MAX4000XL. The effects of various factors such as test temperature, drying profile, end point criteria, lift compensation, chamber configuration, and rehydration on residual moisture (RM) are examined. The performance of the RMAs is based on their ability to reproduce RM results obtained by the current standard gravimetric method. RMAs provide reliable, accurate and reproducible results in a number of industries that rely on the determination of RM. We hypothesize that RMAs are suitable for measuring RM in DBM and provide validation study data with optimized settings for these two instruments. Potentially, such studies will provide justification for allowance of this methodology as an acceptable alternative to the current gravimetric method allowed by American Association of Tissue Banks Standards.

An efficient process is developed by spin‐coating a single‐component, self‐assembled monolayer (SAM) to simultaneously modify the bottom‐contact electrode and dielectric surfaces of organic thin‐film transistors (OTFTs). This effi cient interface modifi cation is achieved using n‐alkyl phosphonic acid based SAMs to prime silver bottom‐contacts and hafnium oxide (HfO2) dielectrics in low‐voltage OTFTs. Surface characterization using near edge X‐ray absorption fi ne structure (NEXAFS) spectroscopy, X‐ray photoelectron spectroscopy (XPS), attenuated total reflectance Fourier transform infrared (ATR‐FTIR) spectroscopy, atomic force microscopy (AFM), and spectroscopic ellipsometry suggest this process yields structurally well‐defi ned phosphonate SAMs on both metal and oxide surfaces. Rational selection of the alkyl length of the SAM leads to greatly enhanced performance for both n‐channel (C60) and p‐channel (pentacene) based OTFTs. Specifi cally, SAMs of n‐octylphos‐phonic acid (OPA) provide both low‐contact resistance at the bottom‐contact electrodes and excellent interfacial properties for compact semiconductor grain growth with high carrier mobilities. OTFTs based on OPA modifi ed silver electrode/HfO2 dielectric bottom‐contact structures can be operated using < 3V with low contact resistance (down to 700 Ohm‐cm), low subthreshold swing (as low as 75 mV dec−1), high on/off current ratios of 107, and charge carrier mobilities as high as 4.6 and 0.8 cm2 V−1 s−1, for C60 and pentacene, respectively. These results demonstrate that this is a simple and efficient process for improving the performance of bottom‐contact OTFTs.