Natural rubber (NR) isolated from Hevea Brasiliensis was investigated by differential scanning calorimetry, dielectric spectroscopy, and high-pressure dielectric spectroscopy. In the range of frequencies (5 × 10−2 to 3 × 106 Hz), temperatures (−120 to 120 °C), and pressures (0.1 to 240 MPa) studied, the dielectric spectra exhibit two overlapped α-processes but no subglass relaxations. Thermal measurements revealed the presence of some moisture in NR. To elucidate the influence of water, dielectric measurements were carried out in dry and wet NR samples. The origin of the two dielectrically active processes was discussed in terms of (i) the apparent activation volume, (ii) the pressure coefficient of the respective glass temperatures, and (iii) the values of the ratio of activation energies, at constant volume and pressure. The latter allowed extracting the relative contribution of thermal energy and volume for each dynamic process. On the basis of these results, the faster α-processes is assigned to the rigidified rubber backbone dynamics whereas the slower to fatty acids (such as stearic acid) that are linked to the rubber chain.
ElsevierOrtiz Serna, MP.; Díaz Calleja, R.; Sanchis Sánchez, MJ.; Riande, E.; Numes, R.; Martins, A.; Visconte, L. (2011) AbstractNanocomposite materials obtained from natural rubber (NR) reinforced with different amounts of cellulose II nanoparticles (in the range of 0 to 30 phr) are studied by dielectric spectroscopy (DS) in the high temperature range (50 to 150 ºC). The obtained spectra exhibit conductivity phenomena at low frequencies and high temperatures. The samples were also studied in the dry state. For comparative purpose the pure materials, NR and cellulose, are also investigated. An explanation is given concerning the cellulose effect on the conductive properties of the dry and wet nanocomposites.
ABSTRACT:The effect of recycled PP on incompatible blends of virgin polypropylene (PP) and high-density polyethylene (HDPE) was studied. Recycled PP from urban solid waste was extracted with methyl ethyl ketone and the compatibilizing action of the product before and after extraction was examined. The characterization of the recycled PP was performed by FTIR, NMR, and DSC analyses. Mechanical properties of the blends were evaluated. The results showed partial compatibility of the blend components, reflected in the improvement of the tensile strength and elongation. Best results were achieved by the addition of extracted recycled PP on the 50/50 PP/HDPE blends.
O estudo do efeito do envelhecimento em artefatos é principalmente importante quanto ao custo e qualidade, tornando o material atrativo ou não para produtos expostos a condições climáticas mais exigentes. Neste trabalho foi estudado o efeito do envelhecimento acelerado em composições vulcanizáveis de borracha natural com mica. O teor da carga mineral variou entre 0 e 40phr. As diferentes composições foram avaliadas, antes e após envelhecimento, quanto às propriedades mecânicas e dinâmico-mecânicas, e também quanto à densidade de ligações cruzadas. Todos os dados foram comparados aos da composição sem carga. Os resultados mostraram que o teor de mica na formulação estudada, antes e após envelhecimento, não deve ser superior a 30phr. Pôde também ser concluído que as características da mica foram as responsáveis pela resistência ao envelhecimento das composições de borracha natural, nas condições escolhidas. As propriedades dinâmico-mecânicas, obtidas por DMTA, corroboraram as propriedades mecânicas avaliadas.
O balanço das reações de reticulação e cisão em cadeias poliolefínicas, quando expostas a condições ambientais de radicais livres, pode resultar em boas propriedades e novas aplicações. Materiais descartados de alta qualidade despertam cada vez mais interesse para reciclagem. Os resíduos plásticos de embalagens alimentícias, assim como peças descartadas de grandes dimensões, provenientes da indústria automotiva, são exemplos daqueles materiais. No presente trabalho, são relatadas as propriedades mecânicas da madeira plástica IMAWOOD, obtida a partir de resíduos sólidos urbanos, principalmente embalagens de polietileno, e do material IMACAR, recuperado de pára-choques descartados de carros de passeio, constituído basicamente de misturas PP/EPDM. Verificou-se que o IMAWOOD mostrou comportamento mecânico melhorado por efeito da radiação-gama, enquanto que o IMACAR revelou alta resistência ao impacto, muito superior ao material virgem de composição correspondente.
Neste trabalho foi estudada a influência da adição de mica em composições vulcanizáveis de borracha natural quanto às propriedades mecânicas e dinâmico-mecânicas. As diversas composições também foram avaliadas quanto à densidade de ligações cruzadas. Todos os dados foram comparados aos da composição sem carga. Os resultados mostraram que a adição de teores crescentes de mica na borracha natural aumentou o módulo a 300%, a dureza, a densidade de ligações cruzadas e a deformação permanente à compressão (DPC) das composições, por outro lado diminuiu a resiliência e a resistência à abrasão. O melhor desempenho quanto à resistência ao rasgamento e à tensão na ruptura foi obtido com 30phr de mica. As propriedades dinâmico-mecânicas (DMTA) corroboraram as propriedades mecânicas obtidas.
Vulcanized composites of chloroprene rubber (CR) with cellulose II (Cel II) as a filler were investigated. Cel II, obtained by the coagulation of cellulose xanthate, was incorporated in the rubber by the traditional method. The filler content varied from 0 to 30 phr. For comparison purposes, carbon black (CB)-CR composites were also studied. The CB amount varied from 0 to 45 phr. The mechanical and dynamic mechanical properties were determined, and the CR composite containing 20 phr of Cel II showed the best set of properties.
Resumo: Aplicações de artefatos de borracha muitas vezes requerem um conjunto de propriedades que não podem ser fornecidas por um único elastômero sendo, então necessário, que misturas de dois ou mais polímeros sejam empregadas. Nesses casos, os demais ingredientes que normalmente são adicionados, distribuem-se de modo diferente dependendo de sua afinidade com cada uma das borrachas. O grau de dispersão de cada um desses ingredientes em cada fase elastomérica irá influenciar a velocidade e o grau de vulcanização e, certamente, terá conseqüências sobre o desempenho do composto final. Neste trabalho, a borracha natural (NR) foi misturada ao elastômero de butadieno-estireno (SBR) na proporção de 1:1 em peso. As composições foram preparadas em misturador de cilindros, segundo a norma ASTM D 3182, empregando-se quatro maneiras distintas para a incorporação dos aditivos. Após a vulcanização foram estudadas propriedades mecâni-cas, como resistências à tração e ao rasgamento e dureza, propriedades termo-dinâmico-mecânicas e a morfologia de cada uma das composições. As propriedades mecânicas foram avaliadas de acordo com as normas ASTM específicas para cada ensaio. Os resultados mostram que, apesar de se usar a mesma formulação, o modo de preparo tem grande influência sobre as propriedades, o que é detectável pelas propriedades mecânicas e pela análise morfológica, e evidenciado através de testes sensíveis, como o dinâmico-mecânico. No caso da mistura NR/SBR as melhores propriedades são obtidas quando é favorecida a vulcanização da borracha que, isoladamente, apresenta propriedades inferiores. Palavras-chave: Mistura de elastômeros, propriedades mecânicas, análise termo-dinâmico-mecânica. NR/SBR Blends: Preparation Modes and PropertiesAbstract: Frequently a set of properties required for a given application cannot be accomplished by only one elastomer and, thus, mixtures of two or more polymers must be employed. In these cases, the other ingredients normally added are dispersed differently, depending on their affinity to each polymer. The degree of dispersion each additive experiences in each elastomeric phase will influence the rate and the degree of vulcanization and will certainly have consequences on the performance of the final product. In this work, natural rubber (NR) was mixed to butadiene-styrene elastomer (SBR) in a 50:50 w/w ratio. The compositions were prepared in a two-roll mill, according to ASTM D3182, introducing the additives in four different modes. After vulcanization, the mixes were investigated as for their mechanical (stress and tear strengths and hardness), dynamic mechanical thermal and morphological analysis. Mechanical properties were evaluated according to ASTM procedures, specific for each test. The results show that, although having been prepared following the same formulation, the properties of these mixtures are influenced by the preparation mode, which could be detected by mechanical and morphological analysis and evidenced through more sensitive methods as DMTA. For NR/SBR blends, the bes...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
334 Leonard St
Brooklyn, NY 11211
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.