OBJECTIVE: The objective of this study was to assess, in vitro, the influence of bleaching gel and the use of desensitizing agent over bond strength of ceramic brackets bonded to bovine enamel. METHODS: One hundred bovine incisors were selected and randomly divided into five groups (n = 20): Group 1, control group (without bleaching); Group 2, bleached with 35% hydrogen peroxide; Group 3, bleached with 35% hydrogen peroxide (three applications, 15 minutes each) and desensitizing agent applied for 10 minutes; Group 4, bleached with 35% hydrogen peroxide for 40 minutes; Group 5, bleached with 35% hydrogen peroxide for 40 minutes with desensitizing agent applied for 10 minutes. Brackets were bonded 7 days after bleaching and submitted to shear bond strength test after 24 hours at a compression rate of 1 mm/minute. After fracture, the adhesive remnant index (ARI) was assessed under stereoscopic at 40 x magnification. Shear strength data (MPa) were submitted to one-way ANOVA and Tukey's test with significance level set at 5%. RESULTS: Group 5 (29.33 MPa) showed significantly higher bond strength than Group 1 (19.19 MPa), Group 2 (20.59 MPa) and Group 4 (23.25 MPa), but with no difference in comparison to Group 3. There was no significant difference among the other groups. The adhesive remnant index showed predominance of score 3, that is, all resin remained adhered to enamel for all groups. CONCLUSION: Bleaching with 35% hydrogen peroxide with calcium associated with desensitizing agent application produced higher bond strength values of brackets bonded to bovine enamel.
The treatment of skeletal disharmonies presents better results when performed during the growth period. The physical changes that occur in every individual express growth, which is ruled by genetic, general and environmental factors. In order to identify such disharmonies and hence concentrate the clinical actions during treatment and influence facial growth, cephalometrics appears as a useful a diagnostic tool for identifying facial growth patterns or growth direction. Jarabak's cephalometric analysis is used to assess facial growth pattern of subjects with normal occlusion or malocclusions. The purpose of this study was to obtain mean values for cephalometric measurements from Jarabak's cephalometric analyses of black Brazilian subjects resident in the city of Piracicaba, São Paulo state, Brazil and vicinities, who presented Class I molar relationship with normal overjet and overbite, mild or no tooth crowding or spacing, and no history of orthodontic treatment. A sample of 37 stone plaster casts and 37 lateral teleradiographs from both male and female individuals aged 10 to 14 years was evaluated. Data were analyzed statistically by Student's t-test at 5% significance level. There was no significant differences between genders. The cephalometric measurements obtained in this study were similar to the Jarabak's standards, except for S-N mean value in females (66.50 mm +/- 3.16), which was significantly lower than the standard.
ResumoIntrodução: Os elásticos corrente são acessórios indispensáveis no tratamento ortodôntico, e suas propriedades de grande interesse para o profissional, a fim de obter maior controle sobre os movimentos dos dentes. Objetivo: Avaliar a influência da marca comercial e comprimento da cadeia espaçadora de elásticos corrente na degradação de força. Material e método: Foram utilizadas ligaduras elásticas ortodônticas em cadeia, tipo curto, médio e longo das marcas: Rocky Mountain (RMO), TP e GAC. Os elásticos, contendo elos correspondentes a 12,5 mm, foram tensionados entre pinos de aço na máquina de ensaio universal Instron 4411 até 25 mm. O valor foi anotado. Após a aferição inicial da força, os elásticos foram fixados em placa de resina acrílica e mantidos distendidos a 25 mm. Foram inseridas em recipiente contendo água deionizada e mantidas em estufa a 37 °C. A leitura da força dos elásticos foi feita nos tempos de 24 horas, 48 horas, 7 dias, 14 dias, 21 dias e 28 dias. Os dados foram submetidos ao teste estatístico apropriado, com nível de significância de 5%. Resultado: Os elásticos TP apresentaram força significativamente maior em todos os períodos. Os elásticos GAC e RMO apresentaram forças estatisticamente semelhantes. Os elásticos TP cadeia curta e longa apresentaram força significativamente maior que os elásticos cadeia média. Para GAC e RMO os elásticos curto apresentaram força maior que os médios e este maior que os longos. Conclusão: A cadeia espaçadora e a marca comercial influenciaram nos resultados obtidos, reforçando a importância do conhecimento dos tipos de elástico.Descritores: Elastômeros; ortodontia; elasticidade. AbstractIntroduction: Elastic chains are indispensable accessories in orthodontic treatment. Changes in their properties are of great interest to professionals in order to gain greater control over tooth movements. Objective: Evaluate the influence of trademark and length of the spacer chain on force degradation of elastic. Material and method: We used the following elastic chain types: TP, Rocky Mountain (RMO) and GAC short, medium and long varieties. The elastics, which contained links corresponding to 12.5 mm, were tensioned between steel pins using Instron 4411 universal testing machine up to 25 mm. The value was recorded. After initial measurement of the force, the elastics were fixed on an acrylic resin plate and kept distended to 25 mm. They were inserted in a container with deionized water and kept in an incubator at 37º. The elastic force data was collected at time intervals of 24 hours, 48 hours, 7 days, 14 days, 21 days and 28 days. These records were subjected to an appropriate statistical test, with significance level of 5%. Result: TP elastics showed significantly higher force in all periods. RMO and GAC elastics showed similar elastic forces. Short and long TP elastics exhibited significantly higher strength than the average elastic chain. As regards GAC and RMO, short elastics showed higher than average force values, and higher values than the long type. Conclusion...
Aim:To evaluate the force decay of orthodontic elastomeric chains after immersion in disinfecting solutions. Methods: One-hundred and fifty segments of elastomeric chains were divided in 3 groups: Control group -no disinfection; Chlorhexidine group -disinfection in 0.12% chlorhexidine digluconate solution; and Peracetic acid group -disinfection in 0.2% peracetic acid solution. Elastomeric chains of 14 mm were stretched up to 20 mm and the given force (kgf) was evaluated in an Instron universal testing machine at the following intervals: 1 h, 1 day, 7, 14, 21 and 28 days after the immersion in the disinfecting solutions. Data (kgf) were analyzed statistically by Analysis of Variance and Tukey's test at a 5% significance level. Results: Both groups presented similar force decay along 7 days and remained stable up to 28 days. Force degradation was observed in the first hours of activation (~50%). Conclusions: It may be concluded that there were no significant differences among the investigated groups, in most interval times, indicating that both chemical solutions can be used for previous disinfection of orthodontic elastomeric chains.
The aim of this study was to evaluate the shear bond strength (SBS) of metallic orthodontic brackets bonded to bovine teeth using light-activated or chemically activated composite resins. One hundred and twenty bovine mandibular incisors were divided into 6 groups (n=20), according to the bonding materials: Transbond XT (T); Enforce Dual (ED); Enforce chemical (EC); Enforce Light-activated (EL); Concise Orthodontic (C); and RelyX Unicem Capsule (UN). Metallic brackets were positioned and firmly bonded to the teeth. Lightactivation for T, ED, EL and UN was carried out with four exposures on each side of the bracket with 20 s total exposure times using XL2500 (3M ESPE). EC and C were chemically cured. Next, all specimens were stored in deionized water at 37 °C for 24 h. The shear bond strength was carried out at a crosshead speed of 1.0 mm/min. Data were subjected to one-way ANOVA and Tukey's test (α=0.05). The adhesive remnant index (ARI) was evaluated at 8× magnification. C (17.72±4.45) presented significantly higher SBS means (in MPa) than the other groups (p<0.05), followed by EC (11.97±5.77) and ED (10.57±1.32). EL (5.39±1.06) and UN (4.32±1.98) showed the lowest SBS means, while T (9.09±2.56) showed intermediate values. For ARI, there was a predominance of score 0 for EC, C and UN, and score 3 for T, ED and EL. In conclusion, the activation mode influenced the SBS.
Os objetivos desse trabalho foram determinar, em moradores assistidos pelo Programa Saúde da Família na cidade de Casa Branca – SP, a prevalência de más oclusões e suas relações as com alterações funcionais: respiração e deglutição. O estudo foi realizado na área assistida pela Unidade de Saúde da Família de Casa Branca, num total 652 crianças, de ambos os gêneros e com idade entre sete e quatorze anos. A oclusão foi avaliada de acordo com as relações anteroposterior, vertical e transversal. Para a análise estatística foram utilizados os testes Coeficiente de Correlação, Qui-quadrado e Fisher. Os resultados mostraram que 70,1% da amostra apresentam má oclusão. No aspecto funcional, 9,5% apresentaram respiração bucal e 10% deglutição atípica. Houve correlação positiva estatisticamente significante entre a má oclusão e as duas funções avaliadas (p<0,001). Concluiu-se que a prevalência da má oclusão foi elevada e esta apresentou correlação positiva com as alterações funcionais.
Objective: To evaluate the shear bond strength of lingual orthodontic brackets with resin or metal pads, the location of bond failure and the adhesive remnant index (ARI). Methods: A total of 40 extracted upper premolars were randomly divided into two groups of 20 each: bonding with brackets having (1) pads with extended resin directly on the lingual surface of teeth, and (2) pads with metal custom base on the lingual surface of teeth. The debonding force was measured with an Instron universal testing machine. A Student’s t-test was used to assess the difference between groups (α = 0.05). Results: The results showed a significant difference between the groups (p < 0.001). The shear bond strength of metal pads was significantly higher than resin pads. Conclusions: Within the limitations of this in vitro study, it was concluded that the bond strength of lingual brackets with metal pads was higher than that of brackets with composite resin pads, due to the metal part being a single unit and welded. The failure location in the region between the bracket and the resin pad affected a higher percentage of the resin pads than the metal pads.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.