High quality heating device made of ferromagnetic alloy (thermal seed) was developed for hyperthermia treatment of cancer. The device generates sufficient heat at room temperature and stops heating at the Curie temperature T (c). The power dissipated from each seed was calculated from the area enclosed by the hysteresis loop. A new mathematical formula for the calculation of heating power was derived and showed good agreement with those calculated from hysteresis loop and calorimetric method.
We demonstrate that the promising effect of inclusion of single magnetic-domain type-M hexaferrite of barium (BaM) particles in polystyrene (PS) polymer (BaM/PS weight ratio = 2/1). The results show that the coercivity of BaM particles remarkably increases from 714 to 3772 Oe and remanence increases from 2.07 to 5.41 emu.g−1 when they embedded into PS. Moreover, magnetic coercivity and squareness of the BaM-PS are significantly larger, and is comparable with corresponding values of other BaM-polymer composites. Therefore, BaM-PS composite enforce itself as the modern potential materials with tendency of replacing existing composite materials in several applications.
a b s t r a c tConducting p-type polymer of poly(3,4-ethylene dioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) has been widely used for organic optoelectronics, particularly as a hole transport layer for organic solar cells. While the aged PEDOT:PSS dispersion impacts device performance, the aging of PEDOT:PSS dispersion have not been well investigated. Moreover, the recovery process of aged (two-year-old) PEDOT:PSS dispersion has not been demonstrated yet. Herein, it is found that aqueous PEDOT:PSS dispersion undergoes extensive phase separation during the aging process, resulting in both nanoscale and macroscale hydrophobic PEDOT-rich agglomerates. When the aged PEDOT:PSS thin film is integrated into P3HT:PCBM organic solar cells, the PEDOT-rich agglomerates trap the photogenerated holes at the PEDOT:PSS/P3HT interface, resulting in poor extraction efficiency in organic solar cells. To recover a hole transport functionality from aged PEDOT:PSS, three different solvents such as isopropyl alcohol (C 3 H 7 OH), ethanol (C 2 H 5 OH) and methanol (CH 3 OH) are investigated. Among them, it is found that isopropyl alcohol (IPA) yielded very uniform PEDOT:PSS thin film layer. This is because hydrophobic functional groups of IPA solvent facilitated the preferential solvation of phase separated hydrophobic PEDOT-rich agglomerates. However, when non-optimal concentration of IPA solvents was added into the aged PEDOT:PSS dispersion, the size of PEDOT-rich agglomerates was adversely enlarged. When organic solar cells were fabricated using more than a two-year-old PEDOT:PSS that was treated with IPA solvent, the resulting device performance of organic solar cells was fully recovered and became comparable or better than that of organic solar cells fabricated with fresh PEDOT:PSS.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.