Incorporation of silver nanoparticles in the acrylic resin was evidenced. Moreover, silver was not detected by the detection limit of the atomic absorption spectrophotometer used in this study, even after 120 days of storage in deionized water. Silver nanoparticles are incorporated in the PMMA denture resin to attain an effective antimicrobial material to help control common infections involving oral mucosal tissues in complete denture wearers.
The grafting of maleic anhydride (MA) onto polypropylene (PP) was performed in the presence of the electron-donating monomer styrene (ST) according to a central composite experimental design, in which the initial MA and ST concentrations were varied. The grafting of MA onto PP in the absence of ST was also performed. All reactions were carried out in the molten state in a Haake rheometer. The amount of reacted MA and the extent of degradation in PP were determined by means of Fourier transform infrared spectroscopy and melt flow index (MFI) measure-ments, respectively. The results showed that the presence of ST in the reactive processing caused a reduction in MFI and an increase in the level of reacted MA when the initial MA concentration equaled the initial ST concentration. An increase in the initial MA concentration presented distinct behavior that depended on the ST content.
Resumo: Células a combustível usando membranas poliméricas condutoras de íons representam uma alternativa interessante para substituição de matrizes energéticas convencionais baseadas em combustíveis fósseis e para a geração de energia com mínimo impacto ambiental. Entretanto, as membranas poliméricas atualmente disponíveis apresentam certas propriedades intrínsecas que diminuem a eficiência e a durabilidade sob uso das células construídas, sendo as principais desvantagens o limite de temperatura de uso (devido a necessidade de presença de água para a condução iônica) e suscetibilidade a degradação mecânica, térmica e química. O presente trabalho tem como objetivo a obtenção, caracterização e avaliação do desempenho de membranas poliméricas híbridas baseadas em poli(éter imida) (PEI), um polímero com excelente resistência mecânica e química, e cuja condutividade protônica independe da presença de água, possibilitando o uso a temperaturas mais elevadas. As membranas poliméricas baseadas em poli(éter imida) foram modificadas quimicamente visando o aumento em seu caráter de condutor iônico. A incorporação de um argilomineral com escala nanométrica visou um aumento na resistência mecânica e térmica das membranas obtidas, condições fundamentais para a durabilidade sob uso de células a combustível, além de aumento de propriedades de barreira em relação aos gases de processo. As membranas foram avaliadas por FTIR, DSC, TGA, DMA, densidade, inchamento em água, transmissão de vapor de água e resistência à migração iônica. Os resultados obtidos são promissores, visto que foi possível alterar a propriedade condutora da membrana, sem perdas excessivas na resistência térmica e mecânica. Palavras-chave: Membrana polimérica, nanocompósito polimérico, célula a combustível, eletrólito polimérico. Hybrids Membranes with Potential Use in Fuel Cells -Part 1: Sulphonated Poly (etherimide) NanocompositesAbstract: Fuel Cells based in polymeric membranes are an alternative for the conventional energetic matrices based on fossil fuel and generation of energy with minimum environmental impact. However, polymeric membranes available nowadays for this specific use have some disadvantages, like low efficiency and cell durability. The aim of this work was to prepare and to characterize hybrid polymeric membranes for application as hydrogen fuel cell electrolytes. Membranes based in poly(ether imide) were chemically modified with sulfur groups to increase their ionic conductivity. The incorporation of mineral clay in nanometric scale aims to increase their mechanical and thermal properties. The membranes were evaluated by FTIR, DSC, TGA, DMA, density, hot water uptake, water vapor transmission and ionic migration resistance. The results leaded to a better structure versus properties balance, aiming the high performance of the obtained membranes. Keywords: Polymeric membrane, nanocomposite, fuel cell, polymeric electrolyte. IntroduçãoNos últimos anos, o desenvolvimento de células a combustível tem atraído enorme atenção por parte não somente d...
Resumo: Nanocompósitos de blendas de polietileno de alta densidade (HDPE) com polietileno linear de baixa densidade (LLDPE) e OMMT (montmorilonita organofílica) foram preparados sob fusão em extrusora de duplarosca, utilizando HDPE-g-MA como agente compatibilizante. Os nanocompósitos foram caracterizados através das propriedades térmicas, óticas e de transporte de gases. A blenda HDPE/LLDPE e os nanocompósitos das blendas HDPE/LLDPE como esperado comportam-se como barreira ao vapor de água e são permeáveis ao CO 2 e O 2 . A adição de nanoargila modificou o grau de cristalinidade da matriz polimérica dos nanocompósitos e a diminuição do coeficiente de permeabilidade foi atribuída ao aumento do grau de cristalinidade e do aumento ao caminho difusional para as moléculas do gás passarem pelo filme polimérico. O caminho difusional mais longo devido ao aumento da tortuosidade está relacionado a uma boa dispersão da carga inorgânica, boa molhabilidade desta pela matriz e forte interações na interface. Modelos teóricos de permeabilidade propostos por Nielsen e Bharadwaj foram utilizados para estimar a razão de aspecto da nanoargila nos nanocompósitos e forneceram resultados que se correlacionam bem com as morfologias observadas por microscopia eletrônica de transmissão. HDPE/LLDPE Blend-based Nanocomposites -Part II: Evaluation of Thermal, Optical and Transport PropertiesAbstract: High density polyethylene/ linear low density polyethylene (HDPE/LLDPE) blend-based nanocomposites were prepared in a twin-screw, using HDPE-g-MA as compatibilizer agent. The nanocomposites were characterized through thermal, optical and transport properties. The HDPE/LLDPE blend and the nanocomposites behave as a barrier to water vapor but are permeable to CO 2 e O 2 . The addition of organoclay modified the crystallinity degree of the polymer matrix of the nanocomposites. The reduction of the permeability coefficient of the nanocomposites was correlated to the increase in the crystallinity of the polymer matrix and to the increase in diffusional path of the gas due to the increase in the tortuosity related to a good dispersion of the clay platelets in the matrix. These effects are related also to a good wettability of the filler by the polymeric matrix and strong interactions at the interface. Theorical permeability models proposed by Nielsen and Bharadwaj were used to estimate the aspect ratio of the organoclay in the nanocomposites with correlate well with the images observed through transmission electron microscopy.
Resumo: Membranas poliméricas condutoras de íons têm sido cada vez mais estudadas para o uso em células a combustível. Entretanto, as membranas poliméricas disponíveis no mercado para este fim apresentam algumas limitações de condições de trabalho. Neste estudo o poli(carbonato) modificado quimicamente para uso como membrana condutora de íons foi caracterizado e teve seu desempenho avaliado. A formação de um nanocompósito baseado em sepiolita visou ao aumento na resistência mecânica e térmica das membranas, propriedades, a princípio, prejudicadas pela sulfonação do material. As membranas foram avaliadas por FTIR, DSC, TGA, DMA, inchamento em água, transmissão de vapor de água e resistência à migração iônica. Os resultados mostraram ser possível atingir um balanço estrutura versus propriedades visando a um elevado desempenho das membranas. Palavras-chave: Membrana polimérica, nanocompósito polimérico, célula a combustível, eletrólito polimérico. Hybrid Membranes of Polymer/Clay for Fuel Cell Applications. Part 2. Sulphonated Poly(Carbonate) NanocompositesAbstract: Ion-conducting polymeric membranes have been studied for use in fuel cells. However, polymeric membranes available in the market show some disadvantages. Here we modified polycarbonate chemically for use as ion-conducting membranes, and investigated its performance. The use of the nanoclay sepiolite aimed at improving the mechanical and thermal resistance, which are negatively affected by polymer sulphonation. The membranes were evaluated using FTIR, DSC, TGA, DMA, water swelling, water vapor uptake and ionic migration resistance. The results indicated it to be possible to reach a tradeoff between structure and properties for obtaining high-performance membranes.
Resumo: A despolimerização do poli (tereftalato de etileno) -PET pós-consumo, em solução aquosa 7,5 mol.L -1 de hidróxi-do de sódio foi testado a 100 °C e a 1 atm, com objetivo de obter o ácido tereftálico. O efeito de tensoativos e da concentração da solução sobre o rendimento da despolimerização foi estudado quantitativamente via gravimetria e analises térmica. Excesso de solução alcalina aumenta a velocidade de reação dobrando o rendimento em reações com partículas grosseiras. Os tensoativos DDS e Tween são eficientes na catálise das reações equimolares com partículas grosseiras, mas não afetam as reações com solução alcalina em excesso. Palavras-chave: Despolimerização, PET, reciclagem, tensoativos. Depolymerization of Waste Polyethylene Terephthalate -PET: Effects of Surfactants and Excess of Alkaline SolutionsAbstract: The depolymerization of waste polyethylene terephthalate (PET) in aqueous solutions 7.5 M of sodium hydroxide was tested at 100 °C and 1 atm, in order to obtain the terephthalic acid monomers (TPA). The effect from surfactants and concentration of sodium hydroxide (NaOH) on the reaction extent of depolymerization was studied quantitatively by gravimetric and thermal measurements. Excess of alkaline solution catalyze the reaction and doubled the reaction rate with larger particle size PET. The surfactants DDS and Tween are efficient in catalyzing larger particle size PET under equimolar conditions, but do not affect the reactions under excess of alkaline solution. Keywords: Recycling, PET, depolymerization, tensoatives. IntroduçãoO resíduo sólido gerado pelos centros urbanos é constituído basicamente por papel, papelão, plástico, vidro, resíduos orgâ-nicos, metal e resíduos químicos. A quantidade desses componentes varia de cidade para cidade, sendo que o percentual de material plástico tem aumentado de forma significativa em relação aos outros, principalmente, devido à substituição das embalagens de papel e vidro pelas embalagens plásticas [1] .O poli (tereftalato de etileno) -PET tem como caracterís-ticas básicas a leveza, a resistência e a transparência, propriedades ideais para satisfazer a demanda do consumo domés-tico de bebidas carbonatadas (refrigerantes) e produtos que necessitem de embalagens transparentes e resistentes. A demanda por estes plásticos tem crescido de forma significativa nos últimos anos. O seu índice de reciclagem também é muito alto superando a taxa de reciclagem dos USA e Europa [1,2] .A introdução do PET no setor de embalagens plásticas deu origem a um novo problema ambiental: os grandes volumes deste plástico que são descartados diariamente. Além da poluição visual provocada por esta disposição ao longo das ruas, com as chuvas essas garrafas são arrastadas pela enxurrada até a entrada de galerias pluviais causando o entupimento destas e sérios problemas de inundações.O problema da poluição tem despertado grande preocupação e junto com fatores econômicos (preço do petróleo) estimulam o desenvolvimento da reciclagem destes plásti-cos. Os esforços são no sentido de,...
de cinco sequências de mistura na formação da microestrutura dos nanocompósitos foi estudado. A caracterização estrutural foi realizada por análises de difração de raio X de alto ângulo (WAXD), microscopia eletrônica de transmissão (MET) e comportamento reológico em regime permanente de deformação. Os resultados mostraram que a formação da microestrutura depende da ordem de mistura dos componentes e a utilização de mistura de dois agentes compatibilizantes miscíveis com os constituintes da matriz auxiliou na distribuição da polaridade, facilitando a dispersão das nanoargilas por toda a matriz. Dentre as sequências estudadas, as que a nanoargila foi primeiramente misturada com componentes de menor viscosidade e cristalinidade (LLDPE e/ou LLDPE-g-MA) apresentaram melhor dispersão e distribuição da nanoargila na blenda polimérica. Palavras-chave: Nanocompósitos, HDPE/LLDPE, sequência de mistura. Structural Characterization of HDPE/LLDPE and OMMT Blend-Based Nanocomposites Obtained by Different Blending SequencesAbstract: High density polyethylene/linear low density polyethylene (HDPE/LLDPE) blend-based nanocomposites were prepared in a torque rheometer, using a mixture of HDPE-g-MA and LLDPE-g-MA both containing 1% of maleic anhydride as compatibilizer system. The effect from five blending sequences on the microstructure of the nanocomposites was investigated. The structural characterization was performed through wide angle X-ray diffraction (WAXD), transmission electron microscopy (TEM) and rheological properties. The results showed that the formation of morphology is dependent on the sequence of nanocomposite preparation and that the use of a mixture of two compatibilizer agents, miscible with both components of the blend matrix, facilitated the dispersion of the nanoclay throughout the matrix. The blending sequence where the nanoclay was first mixed with components of lower viscosity and crystallinity (LLDPE and/or LLDPE-g-MA) yielded better distribution and dispersion of nanoclay in the polymer blend. Keywords: Nanocomposites, HDPE/LLDPE, blend sequence. IntroduçãoPoliolefinas, como polietilenos e polipropileno, são amplamente utilizadas em aplicações para embalagens, no setor automotivo e elétrico, onde as propriedades de resistência térmica, mecânica e de permeação a gases possuem grande importância. As propriedades finais dos produtos obtidos a partir de poliolefinas estão intimamente relacionadas à morfologia desses materiais desenvolvida durante o processamento. A grande versatilidade de uso e baixo custo das poliolefinas têm gerado grande interesse tecnológico e científico, principalmente na obtenção de blendas HDPE/LLDPE [1][2][3][4][5][6] . O processamento de HDPE com baixo índice de fluidez é dificultado devido a elevada viscosidade do fundido. A adição de um material com estrutura química semelhante como o LLDPE, com alto índice de fluidez, auxilia no processamento, reduzindo a viscosidade do fundido.Dentre as alternativas utilizadas para melhorar o desempenho mecânico e de barreira das poliolefinas, ...
Resumo: Nanocompósitos de blendas de polietileno de alta densidade (HDPE) com polietileno linear de baixa densidade (LLDPE) e OMMT (montmorilonita organofílica) foram preparados sob fusão em extrusora de duplarosca, utilizando HDPE-g-MA como agente compatibilizante. A caracterização estrutural foi realizada por análises de difração de raios X em alto ângulo (WAXD), microscopia eletrônica de transmissão (MET). Os resultados indicam que a adição do agente compatibilizante favoreceu a formação da microestrutura predominantemente intercalada. Estudos dinâmico-mecânicos mostraram que a adição do agente compatibilizante aumentou as interações entre a carga e a matriz poliolefínica. As diferentes condições de intemperismo as quais os materiais foram submetidos influenciaram no comportamento mecânico dos nanocompósitos de blenda HDPE/LLDPE. Os tratamentos realizados em estufa com circulação forçada de ar e em água proporcionaram o alívio de tensões residuais presentes no sistema, enquanto que o tratamento realizado em câmara de envelhecimento acelerado levou à formação de grupos carbonílicos, de pequena massa molar, que diminuíram o grau de cristalinidade e o módulo elástico dos nanocompósitos. Palavras-chave: Nanocompósitos, HDPE/LLDPE, intemperismo. HDPE/LLDPE Blend-based Nanocomposites -Part I: Evaluation of Thermo-mechanical Properties and Weathering ResistanceAbstract: Nanocomposites from high density polyethylene/ linear low density polyethylene (HDPE/LLDPE) blends were prepared at the melt state in an extruder, using HDPE-g-MA as compatibilizer agent. The structural characterization was performed through wide angle X-ray diffraction (WAXD) and transmission electron microscopy (TEM). The results showed that adding the compatibilizer induced formation of a predominant intercalated microstructure. Dynamic-mechanical studies showed that the addition of the compatibilizer increases the interactions between the nanoclay surface and the polyolefin matrix. The weathering conditions affected the mechanical behavior of HDPE/LLDPE blend-based nanocomposites. Both treatments performed in hot water and in a forced convection air oven provided the relief of residual stresses in the polymer matrix, while the treatment in an accelerated aging chamber provided the formation of carbonyl groups that lead to a decreased degree of crystallinity and elastic modulus of the nanocomposites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
334 Leonard St
Brooklyn, NY 11211
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.