In the field of dental technology, the length of ceramic pontics is limited to avoid mechanical failure. To reduce thermal-induced residual stress within the ceramic, using smaller subcomponents and subsequent bonding with silicate-based glass solder may be a favorable approach. Thus, the bending strength of zirconia compounds bonded with different silicate-based glass solders was investigated. For this purpose, rectangular specimens made of zirconia were bonded by glass solder. Parameters such as the scarf angle (45° and 90°), two different glass solders, as well as the soldering process (pressure and surface treatment) were varied. All specimens were subjected to quasi-static four-point bending tests according to DIN EN ISO 843-1. Additionally, the quality of the glass solder connection was evaluated using μCT and fractography. In the present study, zirconia compounds were sucessful bonded of zirconia compounds using silicate-based glass solder was. No significant differences in terms of bending strength were observed with respect to the different bonding parameters analyzed. The highest bending strength of 130.6 ± 50.5 MPa was achieved with a 90° scarf angle combined with ethanol treatment of the specimens before soldering and an additional application of a pressure of 2 bars in a dental pressure pot before subsequent soldering. Nevertheless, the bending strengths were highly decreased when compared to monolithic zirconia specimens (993.4 ± 125.5 MPa).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.