No abstract

A new family of porous inorganic solids based on nanocrystalline metal oxides is discussed. These materials, made up of 4-7 nm MgO, CaO, Al2O3, ZnO, and others, exhibit unparalleled destructive adsorption properties for acid gases, polar organics, and even chemical/biological warfare agents. These unique sorption properties are due to nanocrystal shape, polar surfaces, and high surface areas. Free-flowing powders or consolidated pellets are effective, and pore structure can be controlled by consolidation pressures. Chemical properties can be adjusted by choice of metal oxide as well as by incorporating other oxides as monolayer films.

No abstract

Towards the utilization of different parts of date palm biomass waste, low-concentration acid-alkali treatment was used to isolate the contained cellulose and α-cellulose. The cellulose yields achieved from the rachis, leaflet, and fiber parts of the biomass were 74.70%, 71.50%, and 73.82%, respectively, while the corresponding α-cellulose yields were 78.63%, 75.64%, and 70.40%, respectively. The cellulose samples were bleached and characterized by thermogravimetric analysis (TGA), Fourier-transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), and X-ray diffraction (XRD). The XRD results revealed high crystallinity of both the cellulose and α-cellulose samples, while the TGA thermograms indicated that the alkali treatment completely removed lignin and hemicelluloses from the rachis. The results of this study demonstrate the promise of using date palm biomass waste as raw material to produce cellulose and α-cellulose.

In the temperature range of 300-500 degrees C, solid nanocrystalline oxides react nearly stoichiometrically with numerous halocarbons, sulfur, and organophosphorus compounds. In some cases, the reaction efficiencies can be improved by the presence of a small amount of transition-metal oxide as catalyst; for example, Fe2O3 on CaO and mobile intermediate species such as FeCl3 or Fe(SO3)x are important in the catalytic process. Herein, a series of environmentally problematic compounds are discussed, including CCl4, COS, CS2, C2Cl4, CHCl3, CH2Cl2, CH3Cl, and (CH3O)2P(O)CH3. Nanocrystals of CaO coated with a thin layer of Fe2O3 (or other transition metals) =[Fe2O3]CaO, or intimately mixed =Fe2O3/CaO were compared with pure CaO. It was found that (a) the presence of a small amount of surface [Fe2O3] or other transition-metal oxide can have a marked effect on the destructive adsorption activity, (b) for some reagents, such as CCl4, C2Cl4, SO2 and others, the nanocrystalline CaO can react in stoichiometric amounts, especially if a transition-metal oxide catalyst is present, (c) although the reaction with dimethylmethylphosphonate is surface-limited, the nanocrystalline calcium oxide performed well and in high capacity, (d) nanocrystalline calcium oxide exhibits near stoichiometric activitywith several interesting sulfur-containing compounds, such as COS and CS2, (e) unfortunately, most fluorocarbons were not destructively adsorbed at 500 degrees C under the conditions employed; however, some of these can be effectively mineralized over the calcium oxide at higher temperatures. These compounds include C2F6, C3F6, C2ClF3, and CHF3, and (f) upon reaction, surface areas decreased considerably, from about 100 to about 10 m2/g. The results of these experiments further demonstrate that, with the proper choice of catalytic material, some solid-gas reactions can be engineered to be rapid and essentially stoichiometric.

No abstract

In this study, leaf and frond date palm waste as feedstock was used to derive biochars. The effects of pyrolysis temperatures on their physical and chemical properties, and their capacity to remove copper, iron, nickel and zinc from single and multi-metal solutions at various pH values were investigated. Analytical and spectroscopic techniques such as scanning electron microscopy, energy dispersive X-ray, Fourier transform infrared spectroscopy, X-ray diffraction, carbon, hydrogen, nitrogen, sulfur elemental analysis, Brunauer Emmett Teller analysis were conducted for characterization. The pore volume, surface area, pH, and total carbon content of date palm leaf and frond biochar increased while functional groups and hydrogen, nitrogen and oxygen content of biochar decreased with increasing pyrolysis temperature compared to feedstock. The removal efficiencies and sorption capacity for single and mixed metal ions were found between 98 and close to 100% and 2.4 and 3.0 mg g− 1 by leaf and frond biochar samples at pH > 6, respectively. Biochar obtained from different feedstock at different pyrolysis temperature did not show any statistically significant improvements on the removal of single or mixed metals from aqueous solutions. The date palm leaf or frond biochar obtained at low pyrolysis temperature is as effective to remove metals as the ones obtained at high pyrolysis temperatures. Therefore, to consume less energy to produce biochar at lower temperature which exhibits same effective removal efficiency will be a win-win solution in terms of sustainability and economy. As a result, date palm waste biochar can be effectively used to remove metals in water and wastewater.

Mesoporous high‐surface‐area alumina was prepared by a modified aerogel procedure. Specific surface areas between 530‐685 m2 g−1 were obtained after heat treatment at 500 °C. Nitrogen adsorption studies have shown that surface areas and pore characteristics change upon decomposition of aluminum hydroxide to oxide as well as upon compaction of oxide powders. The surface area of aluminum hydroxide increased to a maximum, while the pore volume and diameter decreased as the hydroxide was heated to a temperature of 400 °C. Heating at higher temperatures resulted in sintering of the particles accompanied by a decline in the surface area. Compaction of activated alumina into pellets was accompanied by a relatively gradual change in the surface area and pore characteristics at pressures below 6.9×107 Pa, while severe changes took place at a pressure of 1.4×108 Pa. In situ IR studies of the dehydroxylation of the alumina surface, showed ν(OH) absorptions for isolated surface hydroxy groups centering at 3670, 3714, and 3765 cm−1, which are shifted to lower frequencies than common literature values. Pyridine was found to adsorb on Al3+ ions as well as through hydrogen bonding to relatively acidic surface OH groups, and IR spectra indicated the presence of strong Lewis acid sites.