Stir casting is a common metallurgical route in the casting of aluminum composites. Series of work done in this aspect considered the development of the composites with fixed stir casting parameters without applying an optimization approach. These parameters affect the microstructure and performance of the composites. The study is focused on the optimization of the stir casting parameters in the production of Al 7075 reinforced with TiO2 microparticles for performance improvement. Three stir casting parameters of stirring temperature, speed, and time were varied and optimized using the central composite design technique of the response surface method. Properties evaluated were ultimate tensile strength, hardness, impact strength, elastic modulus, and compressive strength. ANOVA results showed that the three stir casting parameters had a significant impact on the property responses. Five quadratic models were established for the properties linking them to the factors. The models were confirmed to be statistically significant at a confidence level of 95% and variations were observed to be < 5%. The interaction profile of the parameters as per response surface was analyzed. Contour plots associated with each interaction gave different ranges of stirring parameters in which each property can be maximized. Simultaneous optimization of the properties using Minitab 19 software showcased 779.3 °C, 574.2 rpm, and 22.5 min as the optimal stir casting parameters for temperature, speed and time respectively.

Bamboo fibers (BF) treated in 1.3 Molar NaOH and particulate coconut shell (PCS) sieved to − 45 µm were incorporated into polyvinyl chloride (PVC) matrix towards improving the properties of PVC composite for ceiling boards and insulating pipes which sags and degrade with time needing improvement in properties. The process was carried out via compression moulding applying 0.2 kPa pressure and carried out at a temperature of 170 °C. Composites developed were grouped according to their composition. Groups A, B, C, and D were infused with 2, 4, 6 and 8 wt% PCS at constant amount, respectively. Each group was intermixed with a varying proportions of BF (0–30 wt% at 5% interval). Tests carried out on the samples produced revealed that the yield strength, modulus of elasticity, flexural strength, modulus of rupture were enhanced with increasing BF proportion from 0 to 30 wt% BF at 2 wt% constant PCS input. Thermal and electrical properties trended downward as the fiber content reduced even as the hardness was enhanced with PCS/BF intermix which was also reflected in the wear loss index. Impact strength was highest on the infix of 4 wt% PCS and 15 wt% BF. Compressive strength was better boasted with increasing fiber and PCS amount but 8 wt% PCS amounted to depreciation in trend. It was generally observed that PCS performed optimally at 2 wt% incorporation while beyond that resulted in lowering of strength. Blending of the two variable inputs; 0–30 wt% BF and 2 wt% PCS presented better enhancement in properties.

Towards developing a polymeric matrix characterized by high strength to cost ratio, polypropylene (PP) was hybridized with low-cost particulate snail shell (PSS) and kenaf fiber (KF) via compression moulding at 180 °C and 0.2 MPa. The developed composites were grouped into three and labeled as mix 2, 4, and 10. Each group entailed the blend of 5, 10, 20, and 30 wt% KF with 2, 4, 10 wt% PSS respectively. From the results, it is observed that the hardness value was enhanced by the blend of 5 to 30 wt% KF and 2, 4, and 10 wt% PSS. However, 2 wt% PSS mix with 5 to 30 wt% KF resulted in progressive improvement in impact, compressive, flexural, and tensile strengths values. The 4 wt% PSS yielded consecutive increase in impact, compressive and flexural strength when combined with 5 and 10 wt% KF. However, it was observed that subsequent addition of 20 and 30 wt% KF led to a marginal reduction in the strength values. The tensile strength attained optimum value when 4 wt% PSS was commixed with 30 wt% KF. Conversely, the combinations of 10 wt% PSS with 5, 10, 20, and 30 wt% KF had no significant improvement to the mechanical properties of PSS/KF-bio-PP composite (except for hardness) siring strength decrease. Taguchi optimization revealed that the collage of 4 wt% PSS and 10 wt% KF presented optimum mix for hybrid bio-PP composite.

No abstract

The present-day structural application requires advanced materials at extreme conditions, and the development of it is not economically feasible. As a result, existing material in the composite form has more visibility to suit the purpose. The material's strengths and qualities must be examined before it can be recommended for use in harsh conditions. In the present study, Al2O3 (3, 6, 9, 12, and 15 wt.%) and ZrO2 particles (2 wt.%) are reinforced with Al-Mg-Si alloy (Al 6061), which possess good isotropic behaviour and better interface bonding. The double stir casting process was adopted for the hybrid composite development, and the samples were cold rolled to reduce grain size and pores in the composites. The developed composites were subjected to mechanical characterisation tests such as hardness, tensile, compression, impact and flexural tests. An increase in reinforcement percentage enhances the mechanical properties. The improvement was attributed to the high thermal mismatch and reduction in the inter-particle distance by cold rolling and the reinforcements. Scanning electron microscope microstructural examination was conducted, and even dispersion of 3 to 15 wt.% Al2O3 reinforcements was observed. Tensile elongation decreases with an increase in reinforcement percentage. High elastic modulus and temperature mismatch between matrix and reinforcements increase the strength of the composites. The fracture behaviour of the composites generally showed dimples which are characteristics of ductile fracture, except at 15 wt.% Al2O3 / 2 wt.% ZrO2 showed a large portion of cleavage planes and grain cracking. The Al-Mg-Si alloy is reinforced with 9 wt%. Al2O3 / 2 wt.% ZrO2 had the best properties suitable for its use in different structural applications.