No abstract

This study evaluated the effect of different finishing-polishing protocols on surface roughness, gloss, morphology and biaxial flexural strength of pressable fluorapatite glass ceramic. Thirty ceramic discs (12x1 mm) were produced and divided into five groups (n=6): CT: control (glaze); DA: fine grit diamond bur; DG: DA + new glaze layer; DP: DA + felt disk with fine grit diamond paste; DK: DA+ sequential polishing with silicon abrasive instruments, goat hair brush and cotton wheel. The specimens were analyzed for surface roughness (Ra) under profilometry and atomic force microscopy (AFM). Gloss was measured with spectrophotometry and micromorphology with scanning electron microscopy (SEM). Flexural strength was assessed by biaxial flexural strength test. Data were analyzed using one-way ANOVA and Tukey’s post hoc test (a=0.05). DK showed the lowest surface roughness values and DA presented the highest in the perfilometer analysis. No significant differences were observed in the AFM for the CT, DG and DK groups, which presented the lower surface roughness; DA and DP had the higher Ra values. The DA, DP and CT showed the lowest surface gloss values, and the reflectance was significantly different from those observed for DK and DG groups. SEM analysis revealed the smoothest surface for DK group, followed by DG and CT groups; DA and DP groups exhibited variable degrees of surface irregularities. No significant differences were observed among groups for the biaxial flexural strength. The polishing protocol used in DK group can be a good alternative for chairside finishing of adjusted pressable fluorapatite glass ceramic surfaces.

No abstract

Silva FP, Faria-e-Silva AL, Moraes RR, Ogliari AO, Reis GR, Oliveira ARF, Menezes MS. Effect of thermally deposited siloxane-methacrylate coating on bonding to glass fibre posts. International Endodontic Journal, 51, 79-85, 2018. Aim To evaluate the alterations promoted by a thermally deposited siloxane-methacrylate coating on the surface of glass fibre posts and their effect on the bond strength of resin-core materials to the posts. Methodology Fibre post surfaces were treated with experimental thermally deposited siloxanemethacrylate coatings or clinically available treatments (i.e. hydrogen peroxide and methylene chloride); nontreated posts were used as controls. The contact angles formed between the post surface and the water/adhesive were measured with a tensiometer. Scanning electron microscopy and electron dispersive spectroscopy were used to examine the topographies and chemical changes in the post surfaces following treatment. Surface roughness was evaluated with laser interferometry. Core resin was bonded to the fibre posts, and microtensile bond strength testing was subsequently performed. The data were individually submitted to ANOVA and Tukey's tests (a = 0.05). Results The water contact angle was reduced significantly (P < 0.05) by the thermally deposited siloxane-methacrylate coating. All treatments significantly increased the adhesive contact angle (P ≤ 0.016) compared to the control as well as the surface roughness (P ≤ 0.006) and the amount of Si on post surfaces. Greater percentages of Si were observed for the thermally deposited coating. The bond strength to the posts was significantly improved by the thermally deposited coating (P < 0.05), whereas the other treatments did not differ from the control. Conclusion Treating the surface of glass fibre posts with a thermally deposited siloxane-methacrylate coating improved the bond strength to resin-based materials. The coating could be performed by manufacturers of glass fibre posts in order to reduce the number of clinical steps required for luting posts into root canals.

No abstract